Abstract:In this study, a novel silicon carbide/platinum/cadmium sulfide (SiC/Pt/CdS) Z-scheme heterojunction nanorod is constructed using a simple chemical reduction-assisted hydrothermal method, in which Pt nanoparticles are anchored at the interface of SiC nanorods and CdS nanoparticles to induce an electron-hole pair transfer along the Z-scheme transport path. Multiple characterization techniques are used to analyze the structure, morphology, and properties of these materials. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) results show that the SiC/Pt/CdS materials with good crystal structure are successfully synthesized. Transmission electron microscopy reveals that Pt nanoparticles grow between the interfaces of SiC nanorods and CdS nanoparticles. UV-Vis diffuse reflectance spectroscopy shows that the as-prepared Z-scheme heterojunction samples have a wider light absorption range in comparison with pristine CdS materials. Photoluminescence spectroscopy and the transient photocurrent response further demonstrate that the SiC/Pt/CdS nanorod sample with an optimal molar ratio possesses the highest electron-hole pair separation efficiency. The loading amount of CdS on the surface of SiC/Pt nanorods is effectively adjusted by controlling the molar ratio of SiC and CdS to achieve the optimal performance of the SiC/Pt/CdS nanorod photocatalysts. The optimal H-2 evolution capacity is achieved at SiC : CdS = 5 : 1 (molar ratio) and the maximum H-2 evolution rate reaches a high value of 122.3 mu mol.h(-1). In addition, scanning electron microscopy, XRD, and XPS analyses show that the morphology and crystal structure of the SiC/Pt/CdS photocatalyst remain unchanged after three cycles of activity testing, indicating that the SiC/Pt/CdS nanocomposite has a stable structure for H-2 evolution under visible light. To prove the Z-scheme transfer mechanism of electron-hole pairs, selective photo-deposition technology is used to simultaneously carry out the photo-reduction deposition of Au nanoparticles and photo-oxidation deposition of Mn3O4 nanoparticles in the photoreaction. The experimental results indicate that during photocatalysis, the electrons in the conduction band of CdS participate mainly in the reduction reaction, and the holes in the valence band of SiC are more likely to undergo the oxidation reaction. The electrons in the conduction band of SiC combine with the holes in the valence band of CdS to form a Z-scheme transport path. Therefore, a possible Z-scheme charge migration path in SiC/Pt/CdS nanorods during photocatalytic H-2 production is proposed to explain the enhancement in the activity. This study provides a new strategy for synthesizing a Z-scheme photocatalytic system based on SiC nanorods. Based on the characterization results, it is determined that SiC/Pt/CdS nanocomposites are highly efficient, inexpensive, easy to prepare, and are stable structures for H-2 evolution under visible light with outstanding commercial application prospects.

Direct Z-scheme CdS-CdS Nanorod Arrays Photoanode: Synthesis, Characterization and Photoelectrochemical Performance

CdS/ZnS Co-Sensitized Hierarchical TiO2Nanotree Array with Rutile/Anatase Junctions for Enhanced Photoelectrochemical Performance

CdS Nanocrystallites Sensitized ZnO Nanorods with Plasmon Enhanced Photoelectrochemical Performance

Fabrication of inorganic–organic core–shell heterostructure: novel CdS@g-C3N4 nanorod arrays for photoelectrochemical hydrogen evolution

Construction of Sugar-Gourd-shaped CdS/Co1-xS Hollow Hetero-Nanostructure As an Efficient Z-scheme Photocatalyst for Hydrogen Generation

Realizing Efficient Photoelectrochemical Performance for Well-Designed CdS@ZnIn2S4 Heterostructure Photoanode with Directional Interfacial Charge Transfer Dynamics

Dodecylamine coordinated tri-arm CdS nanorod wrapped in intermittent ZnS shell for greatly improved photocatalytic H2 evolution

CdS/CdSe core-shell nanorod arrays: energy level alignment and enhanced photoelectrochemical performance.

Construction of Al-ZnO/CdS Photoanodes Modified with Distinctive Alumina Passivation Layer for Improvement of Photoelectrochemical Efficiency and Stability.

Fabrication, Characterization and Photoelectrochemical Properties of CdS/CdSe Nanofilm Co-Sensitized ZnO Nanorod Arrays on Zn Foil Substrate.

Preparation and Photoelectrochemical Properties of CdS Quantum Dot‐sensitized ZnO Nanotube Arrays

Sandwiched ZnO@Au@CdS Nanorod Arrays with Enhanced Visible-Light-driven Photocatalytical Performance.

Sandwiched CdS/Au/ZnO Nanorods with Enhanced Ultraviolet and Visible Photochemical and Photoelectrochemical Properties Via Semiconductor and Metal Cosensitizing

Construction of CdS@ZnO Core–shell Nanorod Arrays by Atomic Layer Deposition for Efficient Photoelectrochemical H2 Evolution

Performance of amine-modified CdS-D@ZIF-8 nanocomposites for enhanced photocatalytic H 2 evolution

Controlled Growth of 3D CdS-Branched ZnO Nanorod Arrays for Efficient Solar Driven Photoelectrochemical Water Splitting

Direct Z Scheme- Fashioned Photoanode Systems Consisting of Fe2O3 Nanorod Arrays and Underlying Thin Sb2Se3 Layers Toward Enhanced Photoelectrochemical Water Splitting Performance

The Co-Decorated TiO2 Nanorod Array Photoanodes by CdS/CdSe to Promote Photoelectrochemical Water Splitting

Constructing Direct Z‐Scheme Heterostructure by Enwrapping ZnIn2S4 on CdS Hollow Cube for Efficient Photocatalytic H2 Generation

Fabrication of Z-Scheme Heterojunction of SiC/Pt/Cds Nanorod for Efficient Photocatalytic H2 Evolution

Double-sided CdS and CdSe quantum dot co-sensitized ZnO nanowire arrays for photoelectrochemical hydrogen generation.