Abstract:Ga-doped ZnO nanowire has a wurtzite hexagonal structure and has been prepared in a horizontal tube furnace by thermal chemical vapor deposition method. In this work, we fabricate the Ga-doped ZnO nanowires without a metalized catalyst through the thermal evaporation of the Zn powers and Ga degrees C.Temperature is the metals at a low growth temperature of 550 d critical experimental parameter for the formation of Ga-dope the ZnO nanowires.This evaporation process can be attributed to Ga dopant In the lattice position of he ZnO nanowires. As shown In scanning electron microscopy (SEM), nanowires of different diameters are evenly arranged on the Si substrate and nucleated via a self-catalysed mechanism by depositing a layer of ZnO film as the crystallization plant before growing ZnO nanowires on the film. Self-catalyzed growth of Ga-doped ZnO nanowires are of diameters 35-150nm and lengths up to several ones of micrometers. High resolution Transmission electron microscope (HRTEM) those lattice image of Ga doped ZnO nanowires, wherein nanowires are seen a lattice of a=3.25 angstrom and c=5.19 angstrom. As determine by selected area diffraction (SAD), the growth direction of Ga-doped ZnO nanowires is [001] and the nanowire consists of single-crystailline ZnO crystals.The luminescence spectra of the Ga-doped ZnO nanowires exhibit a UV band at 374nm and a strong green band at 498nm. In addition, the Ga-doped ZnO nano,wires with different diameters have a larger green light/UV ratio due to the recombination of holes with the electrons occupying the singly ionized more O vacancies that are larger In number. By virue of the doping of Ga, we observe that Ga-doped ZnO nanowires becomes broader and shifts to a longer wave 498nm at a lower energy and a strong green emission as compared to the undoped one in the cathodoluminescence and photoluminescence spectra. The Ga-doped ZnO nanowires; have a greater field-enhancement factor than the undoped ZnO nanowies. The Ga-doped ZnO nanowires with a low turn on field (12V mu m(-1)) are apparently lower than the undoped ZnO nanowires. Our results demonstrate that Ga-doped ZnO nanowires can provide the possibility of application In optoelectric nanodevices.

Znga2o4 Nanotubes With Sharp Cathodoluminescence Peak

Vapor phase growth and photoluminescence of oriented-attachment Zn2GeO4 nanorods array

Facile synthesis of Zn 1−x Cu x O nanorods with a very broad visible band

Growth of Zinc Blende Gaas/Algaas Radial Heterostructure Nanowires by A Two-Temperature Process

From Gan to Znga2o4 Through A Low-Temperature Process: Nanotube and Heterostructure Arrays

Cathodoluminescence and its mapping of flower-like ZnO, ZnO/ZnS core–shell and tube-like ZnS nanostructures

Characterization of Ga-doped ZnO Nanowires Grown by Thermal Chemical Vapor Deposition

Quasi-Aligned Zno Nanotubes Grown on Si Substrates

Optical properties of the ZnO nanotubes synthesized via vapor phase growth

Photoluminescence of Ga-doped ZnO Nanorods Prepared by Chemical Vapor Deposition

Thermal-desorption Induced Enhancement and Patterning of Ultraviolet Emission in Chemically Grown ZnO

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Optoelectronic Properties Of Single-Crystalline Zn2geo4 Nanowires

Preparation and characterization of ZnO nanotubes

Fabrication, Characterization and Field Emission Properties of Large-Scale Uniform ZnO Nanotube Arrays.

Preparation and Cathodoluminescence Properties of Ga-Doped ZnS Nanowalls

Catalyst-Free Two-Step Growth of Quasialigned Znmgo Nanorods and Their Properties

Growth and Spectral Analysis of ZnO Nanotubes

Direct synthesis and strong cathodoluminescence of Al2O3 nanotubes

A Simple Method to Synthesize Β-Ga2o3 Nanorods and Their Photoluminescence Properties

Photoluminescence of ZnO Nanorod-Tio2 Nanotube Hybrid Arrays Produced by Electrodeposition