Abstract:Abstract ZnO flower‐like nanostructures were grown on Ge (100) substrate, by a modified chemical vapor condensation technique of zinc acetate dihydrate at 300 °C, without using any catalyst. These self‐organized three‐dimensional nanostructures were composed of hierarchical arrangement of ZnO nanorods of diameter ∼50 nm around a common nucleus and were distributed uniformly over the entire substrate surface. Evolution study of these structures indicates that the growth begins with a two‐dimensional planar arrangement of 〈0001〉‐oriented ZnO nanorods. With increasing growth time, the expanding adjacent two‐dimensional growth fronts approach each other, followed by which, the formation of three‐dimensional flower‐like structures evolve. Surface diffusion mechanism seems to play an important role in forming these nanostructures, which has been discussed in detail. Elaborate electron microscopic (SEM, TEM) techniques have been used to investigate the growth characteristics of the flower structures. The photoluminescence measurements showed pure free excitonic transition centered at about 3.249 eV with full width at half‐maximum of about 141 meV at 300 K, which blue shifted to 3.361 eV at 10 K with corresponding half width of 7 meV with no defect‐related bandgap peak due to relatively low growth temperature. The optical emission area was imaged through a cathodoluminescence technique. magnified image Scanning electron micrograph of a typical ZnO nanorod flower structure grown at 300 °C on Ge (100).

Vapor phase growth and photoluminescence of oriented-attachment Zn2GeO4 nanorods array

Growth and Formation Mechanism of C-Oriented ZnO Nanorod Arrays Deposited on Glass

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Vapor condensation growth and evolution mechanism of ZnO nanorod flower structures

Thermal-desorption Induced Enhancement and Patterning of Ultraviolet Emission in Chemically Grown ZnO

Growth and optical properties of tetrapod-like indium-doped ZnO nanorods with a layer-structured surface

Island Nucleation, Optical and Ferromagnetic Properties of Vertically Aligned Secondary Growth ZnO : Cu Nanorod Arrays.

Detailed Study on Photoluminescence Property and Growth Mechanism of ZnO Nanowire Arrays Grown by Thermal Evaporation

ZnMgO Nanorod Arrays Grown by Metal-Organic Chemical Vapor Deposition

Chemical Growth of Zno Nanorod Arrays on Textured Nanoparticle Nanoribbons and Its Second-Harmonic Generation Performance

Photoluminescence Characterization of Nanocrystalline ZnO Array

Shape controllable synthesis of ZnO nanorod arrays via vapor phase growth

Growth and Properties of ZnO Nanorod and Nanonails by Thermal Evaporation

Fabrication and Characterization of Highly Oriented N-Doped Zno Nanorods by Selective Area Epitaxy

Nanostructured ZnO: from Monodisperse Nanoparticles to Nanorods

Controllable Growth of Highly Ordered ZnO Nanorod Arrays Via Inverted Self-Assembled Monolayer Template.

Catalyst-Free Two-Step Growth of Quasialigned Znmgo Nanorods and Their Properties

Heteroepitaxial Growth of ZnO Nanorod Arrays on GaAs (111) Substrates by Electrochemical Deposition

Synthesis of two kinds of ZnO nanostructures by vapor phase method

Low-temperature hydrothermally grown 100 μm vertically well-aligned ultralong and ultradense ZnO nanorod arrays with improved PL property

Layer-structured ZnO Nanowire Arrays with Dominant Surface- and Acceptor-Related Emissions