Abstract:Ga-doped ZnO nanowire has a wurtzite hexagonal structure and has been prepared in a horizontal tube furnace by thermal chemical vapor deposition method. In this work, we fabricate the Ga-doped ZnO nanowires without a metalized catalyst through the thermal evaporation of the Zn powers and Ga degrees C.Temperature is the metals at a low growth temperature of 550 d critical experimental parameter for the formation of Ga-dope the ZnO nanowires.This evaporation process can be attributed to Ga dopant In the lattice position of he ZnO nanowires. As shown In scanning electron microscopy (SEM), nanowires of different diameters are evenly arranged on the Si substrate and nucleated via a self-catalysed mechanism by depositing a layer of ZnO film as the crystallization plant before growing ZnO nanowires on the film. Self-catalyzed growth of Ga-doped ZnO nanowires are of diameters 35-150nm and lengths up to several ones of micrometers. High resolution Transmission electron microscope (HRTEM) those lattice image of Ga doped ZnO nanowires, wherein nanowires are seen a lattice of a=3.25 angstrom and c=5.19 angstrom. As determine by selected area diffraction (SAD), the growth direction of Ga-doped ZnO nanowires is [001] and the nanowire consists of single-crystailline ZnO crystals.The luminescence spectra of the Ga-doped ZnO nanowires exhibit a UV band at 374nm and a strong green band at 498nm. In addition, the Ga-doped ZnO nano,wires with different diameters have a larger green light/UV ratio due to the recombination of holes with the electrons occupying the singly ionized more O vacancies that are larger In number. By virue of the doping of Ga, we observe that Ga-doped ZnO nanowires becomes broader and shifts to a longer wave 498nm at a lower energy and a strong green emission as compared to the undoped one in the cathodoluminescence and photoluminescence spectra. The Ga-doped ZnO nanowires; have a greater field-enhancement factor than the undoped ZnO nanowies. The Ga-doped ZnO nanowires with a low turn on field (12V mu m(-1)) are apparently lower than the undoped ZnO nanowires. Our results demonstrate that Ga-doped ZnO nanowires can provide the possibility of application In optoelectric nanodevices.

Preparation and Cathodoluminescence Properties of Ga-Doped ZnS Nanowalls

Synthesis of Two-Dimensional Micron-Sized Single-Crystalline ZnS Thin Nanosheets and Their Photoluminescence Properties

Characterization of Ga-doped ZnO Nanowires Grown by Thermal Chemical Vapor Deposition

Preparation and Photoluminescence of ZnO with Nanostructure by Hollow-Cathode Discharge

Intercrossed Sheet-Like Ga-Doped Zns Nanostructures with Superb Photocatalytic Actvitiy and Photoresponse

Solid Solution, Phase Separation, and Cathodoluminescence of GaP-ZnS Nanostructures.

Preparation and Photoluminescence of Zinc Sulfide Nanowires

Preparation and Cathodoluminescence of Mg‐Doped and Zn‐Doped GaN Powders

Luminescence Characteristics of Impurities-Activated Zns Nanocrystals Prepared in Microemulsion with Hydrothermal Treatment

Photoluminescence of Ga-doped ZnO Nanorods Prepared by Chemical Vapor Deposition

Synthesis and photoluminescence properties of vertically aligned ZnO nanorod–nanowall junction arrays on a ZnO-coated silicon substrate

Synthesis of In-Doped Znga2o4 Nanobelts and Its Enhanced Cathodoluminescence

Field Emission and Optical Properties of Ga-doped ZnO Nanowires Synthesized Via Thermal Evaporation

Synthesis of ZnS Nanowires and Assemblies by Carbothermal Chemical Vapor Deposition and Their Photoluminescence

Optical Properties of Rectangular Cross-sectional ZnS Nanowires

Photoluminescence Properties of Eu3+-Doped Zns Nanocrystals Prepared in A Water/Methanol Solution

The Growth and Optical Properties of Zno Nanowalls

Luminescence Property and Synthesis of Sulfur-Doped Zno Nanowires by Electrochemical Deposition

Preparation and Luminescent Properties of Eu3+-doped Zinc Sulfide Nanocrystals

Synthesis and luminescence properties of chemically synthesized ZnS nanomaterials

Synthesis and Luminescent Modulation of ZnS Crystallite by a Hydrothermal Method