Abstract:Most commercial high-temperature superconducting coated conductors based on ion beam assisted MgO deposited templates use $\mathrm{LaMnO_3}$ (LMO) films as the terminating buffer layer. In contrast, coated conductors based on inclined substrate deposition (ISD)-MgO technology are still produced with homoepitaxial (homoepi)-MgO as the cap layer. In this work we report on the deposition of LMO buffer layers on ISD-MgO/homoepi-MgO by electron beam physical vapor deposition. The growth parameters of textured LMO films were studied systematically and their properties were optimized regarding the critical current densitiy ($J_\mathrm{c}$) of the subsequently deposited $\mathrm{DyBa_2Cu_3O}_{\mathrm{7-}\delta}$ (DyBCO) superconducting films. LMO films without outgrowths at the surface were obtained at growth rates of up to $4\,\mathrm{Å/s}$. Despite the formation of non-stoichiometric LMO films containing $59\,\%$ La, single-phase films were obtained at substrate temperatures below $775^{\circ}\mathrm{C}$ and at oxygen partial pressures of up to $4\times10^{-4}\,\mathrm{mbar}$ due to a large homogeneity region towards La. The $J_\mathrm{c}$ values of DyBCO films deposited on LMO were found to be independent of the LMO thickness in a range from $50\,\mathrm{nm}$ to $450\,\mathrm{nm}$. DyBCO films on LMO reach $J_\mathrm{c}=0.83\,\mathrm{MA/cm^2}$ at $77\,\mathrm{K}$ in zero applied field. This value is up to $30\,\%$ higher than those of DyBCO films grown directly on homoepi-MgO. The wide range of LMO growth parameters and higher $J_\mathrm{c}$ values of DyBCO on LMO compared to DyBCO on homoepi-MgO make this material attractive for its use in manufacturing coated conductors based on ISD-MgO technology.

Multilayer Buffer for High-Temperature Superconductor Devices on MgO

Reduction of strain in high temperature superconductor thin film devices

Epitaxial Thick Film High-Tcsquids

Ultrathin Epitaxial Mgb2 Superconducting Films with High Critical Current Density and T-C above 33 K

Growth of HgBa2CaCu2Oy films with a buffer layer

A Method to Fabricate Biaxially Textured MgO Buffer Layer for HTS Coated Conductor

In Situ Epitaxial MgB2 Thin Films for Superconducting Electronics

Growth of Simplified Buffer Template on Flexible Metallic Substrates for YBa2Cu3O Coated Conductors

Fabrication of YGBCO/STO/YGBCO Trilayer Structure on IBAD-MgO Tape and In-Field Superconducting Property

Hybrid Physical-Chemical Vapor Deposition of Ultrathin Mgb2 Films on Mgo Substrate with High T-C and J(C)

High Tc Superconducting HgBa2CaCu2Oy Films Growth on the YZrO2 Substrates with YBa2Cu3O7 Buffer Layers

Thin Film Magnesium Boride Superconductor with Very High Critical Current Density and Enhanced Irreversibility Field

GROWTH AND PROPERTIES OF SUPERCONDUCTING MgB_2 THIN FILM FABRICATED ON Al_2O_3 SUBSTRATE BY HYBRID PHYSICAL CHEMICAL VAPOR DEPOSITION

Epitaxial Stabilization of an Orthorhombic Mg-Ti-O Superconductor

Y-Ba-Cu-O Superconducting Films Grown on (100) Magnesia and Sapphire Substrates by A Melt Growth Method Without Crucible

Ultrathin MgB2films Fabricated on Al2O3substrate by Hybrid Physical–chemical Vapor Deposition with Hightcandjc

High Thermostability in CoFeB/MgO/Ta Multilayers by {pt(t)/ta(t)} Superlattice Buffer Layers

$\mathrm{La}_{\mathrm{1-}x} \mathrm{Mn}_{\mathrm{1-}y} \mathrm{O}_{\mathrm{1\pm}δ}$ buffer layers on inclined substrate deposited MgO templates for coated conductors

High Thermostability in CoFeB/MgO/Ta Multilayers by {pt(t)/ta(t)}n Superlattice Buffer Layers

MgB2films Fabricated on Molybdenum Substrate by Hybrid Physical–chemical Vapor Deposition for Superconducting RF Cavity Applications

In-field Superconducting Critical Current of Y0.5Gd0.5Ba2Cu3O7-σ Films Obtained by a Multi-Step Deposition Process