Abstract:Platelet‐like anorthite porous ceramics with improved mechanical strength were fabricated via direct gelcasting and firing at 1223‐1473 K using CaCO3, Al(OH)3 and SiO2 powders as the raw materials, along with H3BO3 and melamine sintering/crosslinking agents. Based on DFT calculations, H3BO3 promoted the formation of platelet‐like anorthite at a relatively low temperature via covering the {130} facet of anorthite and reducing the corresponding adsorption energy, which led to the preferential growth along the a ‐ and b ‐axes. The optimal amount of H3BO3 for the anorthite platelet formation was 0.9 wt%. The porous anorthite sample with an original solid content of 22.0 wt%, after firing at 1373 K, contained 71.0% porosity and exhibited a compressive strength as high as 5.7 MPa, which were comparable or even superior to those of porous anorthite ceramics prepared previously at a much higher temperature (1573‐1723 K), indicating that the preparation strategy reported in this paper is feasible in fabricating high‐performance porous anorthite ceramic at a much milder condition. The thermal conductivity of the porous anorthite sample at 1073 K was as low as 0.266 W/(m·K), while the control sample showed a value of 0.645 W/(m·K), suggesting that the former exhibited much lower thermal conductivity value, and thus could be potentially used for thermal insulation at high temperatures.

Fabrication and Characterization of Anorthite Foam Ceramics Having Low Thermal Conductivity

Porous anorthite ceramics with ultra-low thermal conductivity

Anisotropic Porous Ceramic Material with Hierarchical Architecture for Thermal Insulation

Impact of the Mineral Composition and Sintering Temperature on the Synthesis of Anorthite Ceramics

Fabrication and properties of porous anorthite/mullite ceramics

Preparation and characterization of porous anorthite ceramics from red mud and fly ash

Preparation and characteristics of porous anorthite ceramics with high porosity and high‐temperature strength

Effects of Foaming Agent Content on Structure and Properties of Porous Anorthite Ceramics

Mullite Whisker Reinforced Porous Anorthite Ceramics with Low Thermal Conductivity and High Strength

Facile Method for Preparing Hierarchical Al2O3-Glass Foam Ceramics with Superior Thermal Insulating Property.

Porous yttria-stabilized zirconia ceramics with low thermal conductivity via a novel foam-gelcasting method

Low‐temperature preparation of high‐performance porous ceramics composed of anorthite platelets

Synthesis And Growth Of Anorthite Crystal During In Situ Preparation Of Porous Anorthite Ceramics By Foam-Gelcasting

Fabrication of foamed ceramics with enhanced compressive strength and low thermal conductivity via a simple route

Highly Porous Zirconia Ceramic Foams with Low Thermal Conductivity from Particle‐Stabilized Foams

Fabrication of Porous Mullite Ceramics with High Porosity Using Foam-Gelcasting

Pyrochlore-fluorite dual-phase high-entropy ceramic foams with extremely low thermal conductivity from particle-stabilized suspension

Facile Method for Preparing Hierarchical Al 2 O 3 –Glass Foam Ceramics with Superior Thermal Insulating Property

Preparation of foam ceramics from solid wastes: a study on the relationship between firing regime and properties by grey system theory

Preparation of eco-friendly porous ceramic with low thermal conductivity by high-temperature treatment of foamed solid waste based geopolymer with cenospheres

Fabrication and Characterization of Porous Cordierite Ceramics Prepared from Fly Ash and Natural Minerals