Abstract:In this study, a crack-free pyrolysis process of partially cured precursor powder compacts was developed to prepare dense silicon boron carbonitride (SiBCN) monoliths at much lower temperatures (1300 degrees C), thereby circumventing the challenges of sintering densification (> 1800 degrees C). Unlike the elastic fracture in over-cured precursors or the viscoelastic deformation in under-cured precursors, the partially cured precursor, exhibiting elastic-plastic deformation behavior, facilitates limited nanoscale pore formation in a dense structure, achieving a balance between crack-free pyrolysis and densification. Compared to SiBCN derived from the over-cured precursor (sigma = similar to 159 MPa, K-IC = 1.9 MPa center dot m(1/2), Vickers hardness (HV) = 7.8 GPa, and E = 122 GPa), the resulting SiBCN monolith exhibited significantly improved mechanical properties (sigma = similar to 304 MPa, K-IC = 3.7 MPa center dot m(1/2), HV = 10.6 GPa, and E = 161 GPa) and oxidation resistance. In addition, this study investigated the high-temperature performance of SiBCN monoliths, including crystallization and oxidation, and determined the oxidation kinetics induced by pore structure healing and the different oxidation mechanisms of Si-C-N and B-C-N clusters in the amorphous structure. Due to its unique composition and structure, the SiBCN ceramic oxide layer exhibits exceptional self-healing effects on repairing the nanoporous system in the initial stage and shows outstanding high-temperature stability during prolonged oxidation, mitigating adverse effects from bubble formation and crystallization. Due to the nanoporous structure, the oxidation rate is initially controlled by gas diffusion following a linear law before transitioning to oxide layer diffusion characterized by a parabolic law. Finally, due to different valence bond configurations, Si-C-N transforms into an amorphous SiCNO structure after phase separation, unlike the nucleation and growth of residual B-N-C.

Dimethylaminoborane-modified copolysilazane as a novel precursor for high-temperature resistant SiBCN ceramics

High Boron Content and Soluble Polyborosilazanes to Amorphous SiBCN Ceramics

Polyborosilazane with Broadly Tunable Boron Content for SiBCN Ceramics

Polyborosilazane‐Derived High Temperature Resistant SiBCNO

Polymer derived SiBCN(O) ceramics with tunable element content

Hyperbranched polyborosilazanes derived SiBCN ceramic for high-temperature wave-transparent performance

High-Temperature Resistant Polyborosilazanes with Tailored Structures

A linear polycarbosilane containing <i>m</i>-carborane units: Synthesis and characterization as precursor for SiC/B<sub>4</sub>C ceramics

Polyborosilazanes with Controllable B/N Ratio for Si–B–C–N Ceramics

A linear polycarbosilane containing m-carborane units: Synthesis and characterization as precursor for SiC/B4C ceramics

Modification of SiBCN by Zr Atom and Its Effect on Ablative Resistance of Cf/SiBCN(Zr) Composites

Synthesis and Structural Evolution of Dual-Boron-source-modified Polysilazane Derived SiBCN Ceramics

Pseudo low-temperature sintering effect and microstructure evolution of SiBCO ceramics

Preparation and Characterization of Polyborosiloxanes and Their Blends with Phenolic Resin As Shapeable Ceramic Precursors

High-pressure Synthesis, Mechanical Properties and Oxidation Behavior of Advanced Boron-Containing Α/β-Si 3N 4/si Ceramics Using Polymer-Derived Amorphous SiBN Ceramics

Ablation behavior of Csf/SiC‐BN composites with polyborosilazane as sintering aids: High‐temperature damage mechanism

High temperature stable, amorphous SiBCN microwave absorption ceramics with tunable carbon structures derived from divinylbenzene crosslinked hyperbranched polyborosilazane

A novel boron–silicon–alkynyl hybrid copolymer

A novel boron–silicon–alkynyl hybrid copolymer Synthesis, characterization, heat resistance, and thermo-oxidative stabilities

Improved Thermal Stabilities, Ablation and Mechanical Properties for Carbon Fibers/Phenolic Resins Laminated Composites Modified by Silicon-containing Polyborazine

Fabrication of Dense SiBCN Monolith at a Lower Temperature Andits High-Temperature Performance