Abstract:Tungsten fiber-reinforced tungsten composite (Wf/W) material is considered a plasma-facing material (PFM) with good application prospects. Commercial tungsten wire (fiber) prepared through forging and drawing processes has excellent mechanical properties, as well as a very high recrystallization temperature due to the unique texture of it grain structure. Commercial tungsten fiber is the most proper reinforcement for Wf/W. The change in the properties of tungsten fiber because of neutron irradiation makes it inevitable for Wf/W to be used as PFMs. However, there is very little research on the change in the properties of tungsten fiber caused by neutron irradiation. In this work, we used heavy ion irradiation to simulate the displacement damage generated by neutron irradiation to explore the alteration of the properties of a commercial tungsten fiber caused by neutron irradiation. The investigated subject was tungsten fiber with a diameter of 300 μm. The irradiation source was 7.5 MeV Au2+, which generated a maximum displacement damage of 60 dpa at a depth of 400 nm, and the irradiation influenced depth was 1000 nm. Because of the irradiation, significant lattice distortion occurred within the tungsten fiber, resulting in the transition from (110) texture to (100) texture at the fiber’s cross-section. The results of the Schmidt factor and Taylor factor analysis indicate a decrease in the plasticity of the tungsten fiber after irradiation, but it did not completely lose its plasticity. The results of the nanoindentation test confirmed the radiation hardening. After irradiation, the hardness of the tungsten fiber increased by approximately 0.33 GPa, but this increase was relatively small compared to other tungsten-based materials. This indicates that commercial tungsten fiber is a low-cost and highly reliable reinforcement material for Wf/W composite materials.

Effect of Mechanical Milling on the Microstructure of Tungsten under He+ Irradiation Condition

The Effect of A Small Amount of Tungsten on the Microstructure of Mechanically Alloyed Ag37cu63

Long-term Ball Milling and Hot Pressing of In-Situ Nanoscale Tungsten Carbides Reinforced Copper Composite and Its Characterization

The Microstructural and Hardness Changes of Tungsten Fiber after Au2+ Irradiation

Effect of High Temperature Annealing on the Microstructure and Thermal Shock Resistance of Tungsten Coatings Grown by Chemical Vapor Deposition

Effect of Mechanical Milling Time on Helium Irradiation Behavior of W-Nb Alloys

Mechanical Properties and Microstructural Change of W–Y2O3 Alloy under Helium Irradiation

Microstructure and Hardening Effect of Pure Tungsten and ZrO2 Strengthened Tungsten under Carbon Ion Irradiation at 700°C

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Fabrication of nanocrystalline supersaturated W–Al alloys with enhanced thermal stability and high sinterability

Mechanical milling and its influence on microstructure and electric conductivity of high mass fraction TiC / Cu composites

Effect of He Ion Irradiation on the Microstructure of Tungsten at High Temperature

Effect of Y2O3 particles on the helium ion irradiation damage of W-2%Y2O3 composite prepared by wet chemical method

Microstructure Evolution and Effect on Deuterium Retention in TiC- and ZrC-Doped Tungsten under He+ Ion Irradiation

Effect of annealing on the microstructure behavior of D+-irradiated W-2vol.%TiC composite prepared by wet-chemical method

Effect of particle size and high-energy ball milling time on microstructure and mechanical properties of WC-10Co cemented carbides with plate-like WC grains

Mechanical alloying of ODS tungsten heavy alloys and microstructure development of intermetallic compounds

Microstructure and Damage Behavior of W–Cr Alloy under He Irradiation

Microstructure and deuterium retention after ion irradiation of W–Lu2O3 composites

Microstructure and Helium Irradiation Performance of W–ZrC/Sc 2 O 3 Composites Prepared Spark Plasma Sintering

Microstructure Evolution and Effect on Deuterium Retention in Oxide Dispersion Strengthened Tungsten During He+ Irradiation