Abstract:Low-cycle fatigue (LCF) behavior of nickel-based precipitation-strengthened superalloy GH4145/SQ was investigated systematically under fully reversed total strain amplitude control conditions at 538°C in laboratory air. It was shown that the alloy exhibited a pronounced initial fatigue hardening followed by continuous fatigue softening to failure at high strain amplitudes, while at low strain amplitudes the initial hardening was followed by a well-defined saturation stage. Microstructure observations using optical and transmission-electron microscopy revealed that slip band density increased with increasing total strain amplitudes and the size of the γ′precipitates tended to reduction due to repeated shearing by the dislocations with continuous cyclic straining. The above changes in microstructures during cycling were essentially responsible for the fatigue hardening–softening behavior of the alloy. Both optical and SEM micrographs indicated that at low strain amplitudes crack propagation was basically transgranular, while at high strain amplitudes crack propagation was essentially intergranular. Bilinear behavior with a change of slope at a plastic strain amplitude of about 0.2pct was observed in cyclic stress–strain (CSS), Coffin–Manson (C–M) and plastic strain energy–life plots. A change in the number of operating slip systems and the fracture modes with the strain amplitude employed was used to explain this two-slope characteristic. In both the companion specimens test (CST) and the incremental step test (IST) methods the alloy exhibited non-masing type behavior. It was suggested that, for the first approximation, the half-life plastic strain energy could be calculated directly according to the equation without reckoning in the non-masing behavior.

Effect of MCrAlY Coating on the Low-Cycle Fatigue Behavior of a Directionally Solidified Nickel-Base Superalloy at Different Temperatures

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Isothermal LCF Behaviors of a NiCrAlYSi Coated Columnar-Grained Directionally Solidified Nickel Base Superalloy

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Low-cycle fatigue of MCrAlY-coated superalloys: a fracture mechanics-based analysis

Effect of Surface Coating on Low Cycle Fatigue Behavior of Nickel- Based Directionally Solidified Superalloy

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Temperature effect on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

Effect of Aluminide Coating Thickness on High-Temperature Fatigue Response of MAR-M247 Nickel-Based Superalloy

The Effect of Directional Recrystallization on the Low Cycle Fatigue Response of a Powder Metallurgy Nickel-Based Superalloy at Elevated Temperatures

Fatigue behavior of Pt-modified aluminum coated single crystal superalloy at 900 °C

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

Influence of the coating brittleness on the thermomechanical fatigue behavior of a $β$-NiAl coated R125 Ni-based superalloy

Effect of coatings on oxidation behavior of a fourth generation Ni-based single crystal superalloys at ultra high temperature

Microstructural evolution of NiCoCrAlY coated directionally solidified superalloy

Effect of Recrystallization on Low-Cycle Fatigue Behavior of DZ4 Directionally-Solidified Superalloy

Effect of Nickel Aluminide Microcrystalline Coating on High-Temperature Oxidation Behavior of NiAl-33.5%Cr-0.5%Zr Alloy

The effect of the MCrAlY composition and aluminizing cycle upon the microstructure and hot corrosion resistance of the over‐aluminized MCrAlY coating on IN738LC alloy substrate

Microstructural study of aluminide surface coatings on single crystal nickel base superalloy substrates