Abstract:Nickel-based superalloy IN713C produced through investment casting route is widely used for turbocharger turbine wheels in the automotive industry. The produced microstructure and microtexture are not homogeneous across the turbine component due to geometrical factors and localised cooling rate during the casting process, which give rise to inhomogeneous deformation during service. In the present paper, two kinds of in-house fatigue tests, Low Cycle Fatigue (LCF) and High Cycle Fatigue (HCF), were conducted at 600 °C in attempt to simulate the actual fatigue conditions experienced by turbine wheels in turbocharger. From Geometrically Necessary Dislocation (GND) distributions and strain analyses, it is concluded that microstructure heterogeneity such as carbide precipitates distribution within dendritic structure network determine the failure micromechanics during LCF tests. In the early stage of LCF loading, crack principally initiated within near surface carbides that have been oxidised during high temperature exposure. The higher GND density at the tip of carbide precipitates due to oxidation volume expansion are found to facilitate easy cracks initiation and propagation. Moreover, the cluster-like carbides network and its distribution can accelerate oxidation process and crack growth effectively. Furthermore, in the later stage of crack propagation during LCF, the weak interdendrite areas rotate to accommodate increased strain leading to faster cracks propagation and hence final catastrophic failure. Serial section technique for 3-D visualisation was employed to investigate the crystallographic grain orientation correlation with fracture mechanics during HCF loading. It appears that the microtexure and grain orientations are more critical than the alloy microstructure in an area with a relatively uniform carbides distribution and weak dendrite structure where HCF failure occurred. Based on the slip trace analysis, it was found that most faceting occurred in Goss grains (<110>//LD) and on slip system with the highest Schmid factor. It is concluded that cracks were initiated on planes with high Schmid factors and assisted by the presence of porosity.

The Effect of Directional Recrystallization on the Low Cycle Fatigue Response of a Powder Metallurgy Nickel-Based Superalloy at Elevated Temperatures

The Effect of Directional Recrystallization on the Lcf Characteristics of Pm Nickel-Based Superalloy Apk-6

Low cycle fatigue behavior of nickel-based superalloy GH4145/SQ at elevated temperature

Effect of cyclic straining at elevated-temperature on static mechanical properties, microstructures and fracture behavior of nickel-based superalloy GH4145/SQ

Effect of Recrystallization on Low-Cycle Fatigue Behavior of DZ4 Directionally-Solidified Superalloy

Influence of Strain Amplitude on Low-Cycle Fatigue Behaviors of a Fourth-Generation Ni-Based Single-Crystal Superalloy at 980 °C

Effects of Temperature on Superplastic and Fracture Behaviors of a Ni-Co-based Superalloy

Temperature effect on the low cycle fatigue behavior of a directionally solidified nickel-base superalloy

Temperature Effect on Low-Cycle Fatigue Behavior of Nickel-Based Single Crystalline Superalloy

The Effects of Microstructure and Microtexture Generated During Solidification on Deformation Micromechanism in IN713C Nickel-Based Superalloy

Thermomechanical Fatigue of Nickel-Based Single-Crystal Superalloys

Influence of orientation and temperature on the fatigue crack growth of a nickel-based directionally solidified superalloy

High Temperature Low-Cycle Fatigue, Deformation Microstructure and Final Fracture Behavior of a Nickel-Base Superalloy

2D and 3D characterization of oxidation‐fatigue mechanisms in an advanced Ni‐based superalloy: Effects of microstructure and elevated temperature

Temperature Dependence of High-Cycle Fatigue Behavior of a Ni-Base Single Crystal Superalloy

Microstructure evolution and dynamic recrystallization mechanism during thermal deformation of GH4698 superalloy

Dynamic Recrystallization Behavior of a Γ′-Hardened Nickel-Based Superalloy During Hot Deformation

Improved High-temperature Fatigue Performance of Laser Directed Energy Deposited Ni-based Superalloy by Regulating the Heat Treatment

Effect of elevated temperature on high-cycle and very-high-cycle fatigue properties of Ni-based superalloy manufactured by selective laser melting

Thermo-Mechanical Fatigue Behavior of A Single Crystal Nickel-Based Superalloy

Isothermal LCF Behaviors of a NiCrAlYSi Coated Columnar-Grained Directionally Solidified Nickel Base Superalloy