Gas transport property of polyallylamine–poly(vinyl alcohol)/polysulfone composite membranes
Yan Cai,Zhi Wang,Chunhai Yi,Yunhua Bai,Jixiao Wang,Shichang Wang
DOI: https://doi.org/10.1016/j.memsci.2007.10.052
IF: 9.5
2008-01-01
Journal of Membrane Science
Abstract:Polyallylamine (PAAm) was synthesized by free radical polymerization and characterized by Fourier transform infrared resonance (FT-IR) spectroscopy, hydrogen nuclear magnetic resonance (1H NMR) spectroscopy and differential scanning calorimetry (DSC). The composite membranes were prepared by using PAAm–poly(vinyl alcohol) (PVA) blend polymer as the separation layer and polysulfone (PSF) ultrafiltration membranes as the support layer. The surface and cross-section morphology of the membrane was inspected by environmental scanning electron microscopy (ESEM). The gas transport property of the membranes, including gas permeance, flux and selectivity, were investigated by using pure CO2, N2, CH4 gases and CO2/N2 gas mixture (20vol% CO2 and 80vol% N2) and CO2/CH4 gas mixture (10vol% CO2 and 90vol% CH4). The plots of gas permeance or flux versus feed gas pressure imply that CO2 permeation through the membranes follows facilitated transport mechanism whereas N2 and CH4 permeation follows solution–diffusion mechanism. Effect of PAAm content in the separation layer on gas transport property was investigated by measuring the membranes with 0–50wt% PAAm content. With increasing PAAm content, gas permeance increases initially, reaches a maximum, and then decreases gradually. For CO2/N2 gas mixture, the membranes with 10wt% PAAm content show the highest CO2 permeance of about 1.80×10−5cm3 (STP) cm−2s−1KPa−1 and CO2/N2 selectivity of 80 at 0.1MPa feed gas pressure. For CO2/CH4 gas mixture, the membranes with 20wt% PAAm content display the highest CO2 permeance of about 1.95×10−5cm3 (STP) cm−2s−1KPa−1 and CO2/CH4 selectivity of 58 at 0.1MPa feed gas pressure. In order to explore the possible reason of gas permeance varying with PAAm content, the crystallinity of PVA and PAAm–PVA blend polymers was measured by X-ray diffraction (XRD) spectra. The experimental results show an inverse relationship between crystallinity and gas permeance, e.g., a minimum crystallinity and a maximum CO2 permeance are obtained at 20wt% PAAm content, indicating that the possibility of increasing CO2 permeance with PAAm content due to the increase of carrier concentration could be weakened by the increase of crystallinity.