Abstract:New Fe82-85B13-16Si1Cu1 amorphous alloys with low B content and high B/Si content ratios were synthesized by melt spinning for developing good soft magnetic and high strength materials. The crystallization occurs through two stages and the first-stage onset temperature increases from 673 K to 705 K with increasing B content, while the second-stage temperature remains nearly constant. The first and second stages are due to the precipitation of the α-Fe(Si) phase with a size of about 30 nm and the decomposition of the remaining amorphous phase to α-Fe(Si)+Fe3B+Fe2B, respectively. The Fe-based alloys exhibited good soft magnetic properties both in annealed amorphous and nanocrystallized amorphous+α-Fe(Si) phases. The saturated magnetic flux density, coercivity and permeability at 1 kHz are 1.7 T, 4.92 A/m and 7100, respectively, for the annealed amorphous 14B alloy and 1.74 T, 5.62 A/m and 10100, respectively, for the nanocrystallized 13B alloy. The Vickers hardness (H v) is 803–867 for the as-spun state and it increases with decreasing B content. The H v increases significantly by crystallization to α-Fe+amorphous phases and reaches 997–1550 for the alloys annealed at 693–763 K just before T x2. The ultrahigh H v is presumably due to the combination of fine nanoscale mixed phases, high volume fraction of α-Fe(Si) without internal defects and the enrichment of B into the remaining amorphous phase. Such ultrahigh H v has not been obtained for Fe-based amorphous and crystallized alloys before and the addition of 1%Cu is essential for the ultrahigh H v and the amorphous phase formation for the Fe-rich 85%Fe alloy. The new Fe-based alloys are encouraging as future soft magnetic and ultrahigh strength materials with low material cost.

Fe-based Bulk Amorphous Alloys with Iron Contents As High As 82At%

Fe-based Bulk Amorphous Alloys with High Glass Formation Ability and High Saturation Magnetization

Fe65B22Nd9Mo4 bulk nanocomposite permanent magnets produced by crystallizing amorphous precursors

Fe-based glassy alloys with high iron content and high saturation magnetization

Ductile Fe-Based Amorphous Alloys with High Iron Content

Fe-based amorphous alloys with superior soft-magnetic properties prepared via smelting reduction of high-phosphorus oolitic iron ore

Improving the Amorphous Forming Ability and Magnetic Properties of FeSiBPCu Amorphous and Nanocrystalline Alloys by Utilizing Carbon

PREPARATION AND PROPERTIES OF BULK AMORPHOUS Fe-Ni-P-B-Ga ALLOYS

Nanocrystallization, good soft magnetic properties and ultrahigh mechanical strength for Fe82-85B13-16Si1Cu1 amorphous alloys

A unique Fe-based soft magnetic alloy and its magnetic softening mechanism

Effect of Fluxing Treatment on the Properties of Fe 66 Co 15 Mo 1 P 7.5 C 5.5 B 2 Si 3 Bulk Metallic Glass by Water Quenching

The Effects of Si Substitution with C on the Amorphous Forming Ability, Thermal Stability, and Magnetic Properties of an FeSiBPC Amorphous Alloy

Effects of boron content on the structure and magnetic properties of Fe81-xSi13BxMo2Cr1Cu1P2 nanocrystalline alloys

Tailoring Soft Magnetic Properties of Fe-based Amorphous Alloys Through C Addition

Effects of Mo Additions on the Glass-Forming Ability and Magnetic Properties of Bulk Amorphous Fe-C-Si-B-P-Mo Alloys

Design of Fe-based nanocrystalline alloys with superior magnetization and manufacturability

Investigation of glass forming ability, crystallization behavior, and soft magnetic properties of Fe–B–P–C–Cu alloy ribbons

The role of P content on the glass-forming ability and the magnetic properties of FeSiBPC amorphous alloys

Effect of Fe Content on the Soft Magnetic Properties of Fe-Rich FeSiBC Amorphous Alloy

The influence of P on glass forming ability and clusters in melt of FeSiBP amorphous soft-magnetic alloy

Development of high Bs Fe–Ni-based metal amorphous nanocomposite by optimization of glass-forming ability