Abstract:New Fe82-85B13-16Si1Cu1 amorphous alloys with low B content and high B/Si content ratios were synthesized by melt spinning for developing good soft magnetic and high strength materials. The crystallization occurs through two stages and the first-stage onset temperature increases from 673 K to 705 K with increasing B content, while the second-stage temperature remains nearly constant. The first and second stages are due to the precipitation of the α-Fe(Si) phase with a size of about 30 nm and the decomposition of the remaining amorphous phase to α-Fe(Si)+Fe3B+Fe2B, respectively. The Fe-based alloys exhibited good soft magnetic properties both in annealed amorphous and nanocrystallized amorphous+α-Fe(Si) phases. The saturated magnetic flux density, coercivity and permeability at 1 kHz are 1.7 T, 4.92 A/m and 7100, respectively, for the annealed amorphous 14B alloy and 1.74 T, 5.62 A/m and 10100, respectively, for the nanocrystallized 13B alloy. The Vickers hardness (H v) is 803–867 for the as-spun state and it increases with decreasing B content. The H v increases significantly by crystallization to α-Fe+amorphous phases and reaches 997–1550 for the alloys annealed at 693–763 K just before T x2. The ultrahigh H v is presumably due to the combination of fine nanoscale mixed phases, high volume fraction of α-Fe(Si) without internal defects and the enrichment of B into the remaining amorphous phase. Such ultrahigh H v has not been obtained for Fe-based amorphous and crystallized alloys before and the addition of 1%Cu is essential for the ultrahigh H v and the amorphous phase formation for the Fe-rich 85%Fe alloy. The new Fe-based alloys are encouraging as future soft magnetic and ultrahigh strength materials with low material cost.

A unique Fe-based soft magnetic alloy and its magnetic softening mechanism

Design of Fe-based nanocrystalline alloys with superior magnetization and manufacturability

Ductile Fe-based amorphous alloy with excellent soft magnetic properties induced by low-temperature stress annealing

High performance Fe-based nanocrystalline alloys with excellent thermal stability

Fe-B-Si-C-Cu amorphous and nanocrystalline alloys with ultrahigh hardness and enhanced soft magnetic properties

Ultra-fine microstructure and exceptional low coercivity developed in a high-Bs Fe-Si-B-P alloy by co-alloying Ni, Mo, and Cu

Design of FeSiBPCu Soft Magnetic Alloys with Good Amorphous Forming Ability and Ultra-Wide Crystallization Window

Excellent Magnetic Softness-Magnetization Synergy and Suppressed Defect Activation in Soft Magnetic Amorphous Alloys by Magnetic Field Annealing

Structural Origin of Magnetic Softening in a Fe-based Amorphous Alloy Upon Annealing

Nanocrystallization, good soft magnetic properties and ultrahigh mechanical strength for Fe82-85B13-16Si1Cu1 amorphous alloys

Synthesis of Novel FeSiBPCCu Alloys with High Amorphous Forming Ability and Good Soft Magnetic Properties

Exceptionally High Saturation Magnetic Flux Density and Ultralow Coercivity Via an Amorphous–Nanocrystalline Transitional Microstructure in an FeCo‐Based Alloy

Exceptionally High Saturation Magnetic Flux Density and Ultra‐low Coercivity Via an Amorphous‐nanocrystalline Transitional Microstructure in a FeCo‐based Alloy

Excellent Soft Magnetic Properties and Enhanced Glass Forming Ability of Fe-Si-B-C-Cu Nanocrystalline Alloys

Tailoring Soft Magnetic Properties of Fe-based Amorphous Alloys Through C Addition

A Plastic Iron-Based Nanocrystalline Alloy with High Saturation Magnetic Flux Density and Low Coercivity Via Flexible-Annealing

New Fe–Co–Ni–Zr–B Amorphous Alloys with Wide Supercooled Liquid Regions and Good Soft Magnetic Properties

Soft Magnetic Fe-Si-B-Cu Nanocrystalline Alloys with High Cu Concentrations

Minor-Cu Doped Soft Magnetic Fe-based FeCoBCSiCu Amorphous Alloys with High Saturation Magnetization

Superior Magnetic Softness at Elevated Temperature of Si-Rich Fe-Based Nanocrystalline Alloy

Improving the Amorphous Forming Ability and Magnetic Properties of FeSiBPCu Amorphous and Nanocrystalline Alloys by Utilizing Carbon