Abstract:The development of high-speed aerial vehicles urgently requires high-performance integrated materials for ablation resistance, thermal insulation and oxidant protection under high temperature. The previously prepared carbon aerogel composites (C/CA), with ultra-high temperature thermal insulation properties, were impregnated with SiCO precursor sol and pyrolysed in nitrogen atmosphere at 1200?C. The impregnation/pyrolysis process was performed once, twice and thrice to obtain three different C/C-SiCO nanoporous ceramic composites. Further, TaSi2-MoSi2-borosilicate glass (TM-BG) coating or TaSi2-MoSi2-ZrB2-borosilicate glass (TMZBG) coating was prepared on the surface of the C/C-SiCO through slurry brushing combined with graphite powder embedded sintering process. By simulating the actual application environment through oxygen acetylene flame ablation test, the ablation resistance of the samples was studied and their oxidation mechanism was analysed. The results show that the ablation rate of the C/C-SiCO after 200 s ablation at 1600 ?C decreases with the increase of the number of impregnation/pyrolysis steps and that the ablation resistance of the coating modified C/C-SiCO was significantly enhanced. The addition of ZrB2 to the coating improves the compatibility between the substrates and the coating, and the TMZ-BG coated sample has better ablation resistance. At high temperature, the borosilicate glass in the coating is in a viscous flow state. Meanwhile the SiO2 generated by the oxidation of other silicide raw materials forms a dense glass layer on the coating surface, which can be used as an oxygen barrier to provide better protection for the substrates. The coating-modified C/C-SiCO porous ceramic composites are expected to be used as a high-temperature ablation-resistant material for the thermal protection system of new aerospace vehicles.

Microstructure and Oxidation Protection of Borosilicate Glass Coating Prepared by Pulse Arc Discharge Deposition for C/C Composites

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Deposition voltages on the phase evolutions, microstructures, and oxidation behaviors of thermal-resistance Glass-MoSi2-SiC coating

ZrB2 particles reinforced glass coating for oxidation protection of carbon/carbon composites

A Thick SiC-Si Coating Prepared by One-Step Pack Cementation for Long-Term Protection of Carbon/carbon Composites Against Oxidation at 1773 K

A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

Multi-composition Coating for Oxidation Protection of Modified Carbon-Bonded Carbon Fiber Composites

An oxidation protective coating prepared by SiC densifying HfB2-SiC skeleton for SiC-coated C/C composites at 1473, 1773, and 1973 K

Thermal Protection and Dielectric Properties of Borosilicate Coatings for SiCf/SiC Composites Under High-Temperature Oxidation

A gradient composite coating to protect SiC-coated C/C composites against oxidation at mid and high temperature for long-life service

Effect of Al2O3 addition on the microstructure and oxidation behavior of SiC coating prepared by pack cementation on C/C composites

Siliconization elimination for SiC coated C/C composites by a pyrolytic carbon coating and the consequent improvement of the mechanical property and oxidation resistances

Interfacial modification and oxidation resistance behavior of a CVD-SiC coating for C/SiC composites

Oxidation behavior and ablation mechanism of Cf/ZrB2-SiC composite fabricated by vibration-assisted slurry impregnation combined with low-temperature hot pressing

Oxidation properties of tri-layer ytterbium-disilicate/mullite/silicon-carbide environment barrier coatings for Cf/SiC composites

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

Improved oxidation and thermal shock resistance of SiC-Si coating with a SiC w /PyC network structure toughened buffer layer

Ablation resistance of C/C-SiCo nanoporous ceramic composites with TaSi2-MoSi2-ZrB2-borosilicate glass coating

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer

High temperature oxidation resistance of Y2O3 modified ZrB2-SiC coating for carbon/carbon composites

Microstructure, Surface Emissivity and Ablation Resistance of Multilayer Coating for Lightweight and Porous Carbon–bonded Carbon Fiber Composites