Thermal Shock Resistance of Thermal Barrier Coatings for Nickel-Based Superalloy by Supersonic Plasma Spraying

Jia Sun,Qian-Gang Fu,Guan-Nan Liu,He-Jun Li,Yong-Chun Shu,Gao Fan

DOI: https://doi.org/10.1016/j.ceramint.2015.04.077

IF: 5.532

2015-01-01

Ceramics International

Abstract:Double-layer thermal barrier coatings (TBCs), including a top ZrO2 layer and an inner CoNiCrAlY layer, were deposited on nickel-based superalloy using supersonic atmospheric plasma spraying (SAPS). Thermal shock resistance of the TBCs between 1200°C and room temperature was investigated. After thermal shock test, the adhesive strength of the coatings was evaluated through scratch test. The SAPS–TBCs present good thermal shock resistance, exhibiting only 0.26% mass gain up to 150-time thermal cycling. Before thermal cyclic treatment, SAPS–TBCs exhibited a strong adhesion with the absence of the thermally grown oxide (TGO) between out and inner layer. With the increasing of thermal cycles, the TGO layer was formed and its thickness firstly increased and then dropped down. The critical load fell down by about 32% for topcoat–bondcoat adhesion (up to 50 cycles) and 35% or so for TBCs–substrate adhesion (up to 150 cycles) compared to the counterpart of as-sprayed specimens. The strain introduced by the existence of TGO and mixed oxides resulted in a varied adhesion for TBCs on nickel-based alloy during thermal cycling.