Thermal shock resistance and failure analysis of La2(Zr0.75Ce0.25)2O7-based TBCs produced by atmospheric plasma spraying

Pan Yang,Dongyan Yang,Enkang Hao,Yulong An,Yuhong Li,Zhiguang Wang
DOI: https://doi.org/10.1016/j.surfcoat.2021.126903
IF: 4.865
2021-03-01
Surface and Coatings Technology
Abstract:High-temperature thermal barrier coatings (TBCs) have important application prospects in the high-performance gas turbine. It is of great significance to study the thermal shock behaviors in improving the reliability and durability of TBCs. In this study, three groups of high-temperature La2(Zr0.75Ce0.25)2O7 (LCZ)-based coatings (LCZ, LCZ/8YSZ and LCZ/CYSZ) were designed and produced by atmospheric plasma spraying. Two cooling ways, water cooling and air cooling, were employed to conduct the thermal shock tests, which facilitates a comprehensive understanding of the thermal shock resistance and the failure mechanisms of LCZ-based TBCs in cyclic thermal shocks. The thermal shock resistance of these coatings was evaluated by thermal cycling lifetime and the failure mechanisms were analyzed in the framework of crack initiation and propagation. Based on the present results, LCZ/8YSZ coating remains intact after 100 air-cooled thermal shock cycles, indicative of remarkable thermal shock resistance. The initiation and propagation of transverse cracks at the interface between the ceramic layer and bond coat result in interface debonding, which is the only failure mechanism of these coatings in air-cooled thermal shock. Except for the interface debonding, in water-cooled thermal shock, the spalling of top coat is another failure mechanism due to the intersection of vertical cracks and interlayer microcracks. The main reasons for the growth of these cracks were also discussed and analyzed in detail.
physics, applied,materials science, coatings & films
What problem does this paper attempt to address?
The paper primarily explores the thermal shock resistance and failure analysis of thermal barrier coatings (TBCs) based on La₂(Zr₀.₇₅Ce₀.₂₅)₂O₇ (abbreviated as LCZ) under different cooling methods. Specifically, the study designed and prepared three different types of LCZ-based TBCs (namely pure LCZ coating, LCZ/8YSZ double-layer coating, and LCZ/CYSZ double-layer coating) using atmospheric plasma spraying technology. The study conducted thermal shock tests using two different cooling methods, water cooling and air cooling, to comprehensively understand the thermal shock resistance and failure mechanisms of these LCZ-based TBCs under cyclic thermal shock. The study found that: - The LCZ/8YSZ coating remained intact after 100 cycles of air cooling thermal shock, showing excellent thermal shock resistance. - Under air cooling thermal shock, the only failure mechanism of these coatings was interfacial debonding caused by the formation and propagation of transverse cracks at the ceramic layer and bond coat interface. - In water cooling thermal shock, besides interfacial debonding, topcoat spallation was another failure mechanism, which was the result of the intersection of vertical cracks and interlaminar microcracks. - The paper also discussed in detail the main reasons for the growth of these cracks. Additionally, the study observed the phase transformation of LCZ coatings under different thermal shock conditions using Raman spectroscopy and pointed out that phase transformation was not the main cause of coating failure. The paper further observed the thickness of the thermally grown oxide (TGO) layer using a scanning electron microscope, confirming that the TGO layer thickness was insufficient to cause coating failure. The primary cause of coating failure was ultimately determined to be crack propagation induced by thermal stress. For LCZ/CYSZ coatings, the failure mechanism in both thermal shock tests was interfacial debonding; whereas for LCZ/8YSZ coatings, the failure mechanism in water cooling thermal shock was topcoat spallation. In summary, the study aims to develop new high-temperature thermal barrier coating materials suitable for high-performance gas turbines and experimentally investigates the thermal shock performance and failure mechanisms of these coatings.