Abstract:The oxidation of bond coat (BC) and interdiffusion between BC layer and superalloys were two mechanisms that contribute to the degradation of thermal barrier coating system (TBCs). The oxidation and interdiffusion of TBCs on single-crystal superalloys were comparatively studied in this work at 950 °C, 1050 °C and 1100 °C over a duration of 1500 h. The results indicated that the thickness of the thermally grown oxide (TGO) progressively increased with the oxidation time and temperature, following a parabolic law. The discontinuous TGO gradually developed into a double-layer structure: the upper layer was a mixed oxide layer, while the lower layer predominantly comprises an Al 2 O 3 layer. Moreover, an interdiffusion zone (IDZ) is formed at the interface between the BC layer and the substrate, with its thickness increasing in response to both temperature and oxidation time. The Cr-rich phases appeared in the IDZ, where Al initially diffused from the BC layer to the substrate, followed by a reverse diffusion process. Simultaneously, Ni and refractory elements diffused from the substrate into IDZ, resulting in the precipitation of the topologically close-packed (TCP) phases and the formation of a secondary reaction zone (SRZ). It has further been shown that Cr-rich phases further diffused into SRZ. Higher oxidation temperatures accelerated the growth of the SRZ and facilitated the transformation of the TCP phases from a blocky to a needle-like morphology. Ultimately, the continuous growth of IDZ and SRZ led to the evolution of the substrate from a monocrystalline to a polycrystalline structure. This study provides valuable data on the microstructural evolution of TBCs and the assessment of their service life.

The Effect of Shot Blasting Abrasive Particles on the Microstructure of Thermal Barrier Coatings Containing Ni-Based Superalloy

Thermal Shock Behavior of Al2O3/TiO2-NiCrBSi Graded Thermal Barrier Coatings Produced by Flame Spraying

The Microstructure of Al2O3/TiO2-NiCrBSi Graded Thermal Barrier Coatings Produced by Flame Spraying

Influences of MCrAlY Coatings and TBCs on Oxidation Behavior of a Ni-Based Single Crystal Superalloy

Different Growth Mechanisms of Alumina on the Surface of NiPtAl and MCrAlY Bondcoatings in EB-PVD TBC System

Effect of Shot Blasting on NiCrAlY Bonding Coating of Thermal Barrier Coatings

Experimental Investigation on High-Temperature Fatigue and Fracture Properties at the Interface Between Thermal Barrier Coatings (tbcs) and Nickel Based Superalloy Substrate

Substrate-constrained Effect on the Stiffening Behavior of Lamellar Thermal Barrier Coatings

Thermal Failure of Thermal Barrier Coating with Thermal Sprayed Bond Coating on Titanium Alloy

Comparative Study on Microstructure Evolution and Failure Mechanisms of Ordinary and Refurbished EB-PVD TBC under Cyclic Oxidation

Study on the Microstructure Evolution of Nano and Micron-size Thermal Barrier Coatings during Thermal Cycling

Multi-layered Thermal Barrier Coatings Fabricated by Plasma-Spraying and Dry-Ice Blasting: Microstructure Characterization and Prolonged Lifetime

Effects of a nano carbide coating fabricated by EB-PVD on the interfacial stability of aluminide coated superalloy

Thermal Failure of Nanostructured Thermal Barrier Coatings with Cold-Sprayed Nanostructured NiCrAlY Bond Coat

Microstructure and Thermal Cycling Behavior of Thermal Barrier Coating on Near-Α Titanium Alloy

Microstructural Stability of a Metallic Thermal Barrier Coatings for Rocket Engine

Thermal shock behaviors and failure mechanisms of EB-PVD thermal barrier coatings using radiant heating

Formation and Behavior of Thermal Barrier Coatings on Nickel-Base Superalloys

Comparative study of temperature-dependent oxidation and interdiffusion behavior on NiCoCrAlYHf-coated nickel-based single-crystal superalloys

Failure of Electron Beam Physical Vapor Deposited Thermal Barrier Coatings System under Cyclic Thermo-Mechanical Loading with a Thermal Gradient

Influence of Composition of TGO on the Thermal Shock Lifetime of Thermal Barrier Coatings with Cold-Sprayed MCrAlTaY Bond Coat