Abstract:Nitrogen-doped TiO2 nanofibres of anatase and TiO2(B) phases were synthesised by a reaction between titanate nanofibres of a layered structure and gaseous NH3 at 400-700 °C, following a different mechanism than that for the direct nitrogen doping from TiO2. The surface of the N-doped TiO2 nanofibres can be tuned by facial calcination in air to remove the surface-bonded N species, whereas the core remains N doped. N-Doped TiO2 nanofibres, only after calcination in air, became effective photocatalysts for the decomposition of sulforhodamine B under visible-light irradiation. The surface-oxidised surface layer was proven to be very effective for organic molecule adsorption, and the activation of oxygen molecules, whereas the remaining N-doped interior of the fibres strongly absorbed visible light, resulting in the generation of electrons and holes. The N-doped nanofibres were also used as supports of gold nanoparticle (Au NP) photocatalysts for visible-light-driven hydroamination of phenylacetylene with aniline. Phenylacetylene was activated on the N-doped surface of the nanofibres and aniline on the Au NPs. The Au NPs adsorbed on N-doped TiO2(B) nanofibres exhibited much better conversion (80 % of phenylacetylene) than when adsorbed on undoped fibres (46 %) at 40 °C and 95 % of the product is the desired imine. The surface N species can prevent the adsorption of O2 that is unfavourable for the hydroamination reaction, and thus, improve the photocatalytic activity. Removal of the surface N species resulted in a sharp decrease of the photocatalytic activity. These photocatalysts are feasible for practical applications, because they can be easily dispersed into solution and separated from a liquid by filtration, sedimentation or centrifugation due to their fibril morphology.

Painting Anatase (TiO2) Nanocrystals on Long Nanofibers to Prepare Photocatalysts with Large Active Surface for Dye Degradation and Organic Synthesis

A facile synthesis of hierarchical TiO2 for dye adsorption and photocatalysis

(001)-Exposed TiO2 Microcrystals Decorated with Few-Layer Nanobelts for Enhanced Photocatalytic Activity

Titania Nanoflowers with High Photocatalytic Activity

Activation of Carbon Cloth and Concurrent Precipitation of Titania Nanowires for Enhanced Adsorption and Photocatalysis Performance

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Surface roughening and top opening of single crystalline TiO2 nanowires for enhanced photocatalytic activity

Construction of Ni-doped Belt-on-belt TiO2 Thin Film to Assist Photodegradation of Rhodamine B in Water

Tuning the Surface Structure of Nitrogen-Doped TiO2 Nanofibres--an Effective Method to Enhance Photocatalytic Activities of Visible-Light-driven Green Synthesis and Degradation.

Fabrication and Photocatalysis of TiO2 Flower-like Nanostructures

Nitrogen-Doped Anatase Titania Nanorods with Reactive {101} + {010} Facets Exposure Produced from Ultrathin Titania Nanosheets for High Photocatalytic Performance

Facile Synthesis and Active Photocatalysis of Mesoporous and Microporous Tio2 Nanoparticles

Highly Water-Dispersible and Easily Recyclable Anatase Nanoparticles for Photocatalysis

Tio2 Nanoparticles with High Ability for Selective Adsorption and Photodegradation of Textile Dyes under Visible Light by Feasible Preparation

Tio2 Nanoflakes Modified With Gold Nanoparticles As Photocatalysts With High Activity And Durability Under Near Uv Irradiation

Synthesis of Ni-doped Anatase TiO2 Single Crystals Loaded on Wood-Based Activated Carbon for Enhanced Photodegradation of Triphenylmethane Dyes

Single-crystalline TiO2 Nanorods: Highly Active and Easily Recycled Photocatalysts

Hexafluorotitanic acid-assisted synthesis of large-sized, ultrathin titania nanosheets as multifunctional and high-performance photocatalysts

Efficient degradation of dye pollutants on nanoporous polyoxotungstate–anatase composite under visible-light irradiation

Preparation of Photocatalytic Anatase Nanowire Films Byin Situoxidation of Titanium Plate

High Photocatalytic and Adsorptive Performance of Anatase-Covered Titanate Nanotubes Prepared by Wet Chemical Reaction