Abstract:N-doped Na2Ti6O13@TiO2 core-shell nanobelts have been successfully synthesized by first mixing Na2Ti3O7 with titanium isopropoxide, and then calcinating with urea in air. A structural evolution from the phase Na2Ti3O7 to Na2Ti6O13 occurred as the TiO6 octahedra in Na2Ti6O13 is more regular. Anatase TiO2 nanoparticles (NPs) with specifically exposed {1 0 1} facets were deposited on the external surface of Na2Ti6O13 nanobelts, forming the closely contacted interface between two components due to the common structural features of TiO6 octahedra in anatase TiO2 and Na2Ti6O13. The reductive {1 0 1} facets could be acted as a possible reservoir of the photogenerated electrons, yielding a highly reactive surface for the reduction of O-2-O-2 center dot- and thus, lowering the recombination rate of photogenerated electron-hole pairs. The anisotropically shaped titanate nanobelts in the obtained composites possessed a higher charge carrier mobility and provided the pathway for quick transport of charge carriers throughout the longitudinal direction to different reaction sites for subsequent reactions. The doped N atoms were mainly located in the crystal lattices of TiO2, giving rise to the visible light response. Owing to the combined effects of hybridization, morphology engineering, and N doping, the obtained composite showed a high stability and an enhanced catalytic activity for the photodegradation of methylene blue (MB) solution under visible light irradiation. In addition, it was found that both an appropriate mass ratio of TiO2 to titanate and a suitable content of doped N were essential for achieving an excellent performance. The present work may provide an insight for the fabrication of delicate composite photocatalysts with a high performance. (C) 2015 Elsevier B.V. All rights reserved.

Nitrogen-Doped Anatase Titania Nanorods with Reactive {101} + {010} Facets Exposure Produced from Ultrathin Titania Nanosheets for High Photocatalytic Performance

Soft-chemical Synthesis of Mesoporous Nitrogen-Modified Titania with Superior Photocatalytic Performance under Visible Light Irradiation

Facile Fabrication of N-doped TiO2 Nanocatalyst with Superior Performance under Visible Light Irradiation

Hydrothermal Growth of Nanorod Arrays and in Situ Conversion to Nanotube Arrays for Highly Efficient Ag-sensitized Photocatalyst

Titania Nanoflowers with High Photocatalytic Activity

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Low Temperature Synthesis of Few-Layer Titanate Nanobelts on Ti Mesh and the Hot-Water Induced Transformations to Highly Photocatalytic Active Titania Nanorods

Surface roughening and top opening of single crystalline TiO2 nanowires for enhanced photocatalytic activity

Large-Scale Preparation Of Ordered Titania Nanorods With Enhanced Photocatalytic Activity

Natural Leaves-Assisted Synthesis Of Nitrogen-Doped, Carbon-Rich Nanodots-Sensitized, Ag-Loaded Anatase Tio2 Square Nanosheets With Dominant {001} Facets And Their Enhanced Catalytic Applications

Balsam-Pear-Like Rutile/Anatase Core/Shell Titania Nanorod Arrays For Photoelectrochemical Water Splitting

(001)-Exposed TiO2 Microcrystals Decorated with Few-Layer Nanobelts for Enhanced Photocatalytic Activity

N-doped Na2Ti6O13@TiO2 Core–shell Nanobelts with Exposed {1 0 1} Anatase Facets and Enhanced Visible Light Photocatalytic Performance

Low-Temperature Growth of a Nitrogen-Doped Titania Nanoflower Film and Its Ability to Assist Photodegradation of Rhodamine B in Water

Hexafluorotitanic acid-assisted synthesis of large-sized, ultrathin titania nanosheets as multifunctional and high-performance photocatalysts

Facile Synthesis of Anatase–Rutile Diphase N-doped TiO2 Nanoparticles with Excellent Visible Light Photocatalytic Activity

Activation of Carbon Cloth and Concurrent Precipitation of Titania Nanowires for Enhanced Adsorption and Photocatalysis Performance

Synthesis of Pt-Loaded Self-Interspersed Anatase TiO2 with a Large Fraction of (001) Facets for Efficient Photocatalytic Nitrobenzene Degradation.

Single-crystalline Rutile TiO2 Nanorod Array on Flexible Ti Substrates for Efficient Photoelectrocatalytic Degradation of Phenol in Water

Low‐Temperature Transformation of Titania Thin Films from Amorphous Nanowires to Crystallized Nanoflowers for Heterogeneous Photocatalysis

Surface Defect-Controlled Growth and High Photocatalytic H-2 Production Efficiency of Anatase TiO2 Nanosheets