Hexafluorotitanic acid-assisted synthesis of large-sized, ultrathin titania nanosheets as multifunctional and high-performance photocatalysts

Yong-Sheng Jin,Peng Wang,Shu-Hua Teng

DOI: https://doi.org/10.1088/1361-6528/ab9da6

IF: 3.5

2020-07-22

Nanotechnology

Abstract:A fast cyclohexanol solvothermal pathway was developed to prepare highly dispersed anatase titania (TiO₂) nanosheets with an edge length of ~800 nm and a thickness of ~6 nm. Under the synergistic control of hexafluorotitanic acid and cyclohexanol, the exposed 001 facets reached ~98.5% on the TiO₂ nanosheets obtained by the treatment at 180 °C for 150 min. Moreover, it was found that the phase transformation and structural development drastically occurred during the solvothermal treatment. When used as a catalyst for photodegradation of rhodamine B, the TiO₂ nanosheets exhibited a good recycling stability and a much higher photocatalytic degradation rate (nearly 99% degradation within 2.5 h) than the commercial P25 (93.6%). After being uniformly loaded with 4 wt.% of the Pt nanoparticles, the TiO₂ nanosheets displayed a photocatalytic hydrogen production rate of 2.239 mmol g⁻¹ h⁻¹ under simulated solar light, which was much higher than the pristine TiO₂ nanosheets (0.045 mmol g⁻¹ h⁻¹) as well as most of the reported TiO₂-based photocatalysts. The remarkable photocatalytic activity and good stability of the TiO₂ nanosheets with highly exposed 001 facets would make them find potential applications in both water treatment and hydrogen generation from water splitting under solar light.

materials science, multidisciplinary,physics, applied,nanoscience & nanotechnology