Abstract:In the current work, the yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) have been fabricated by atmospheric plasma spraying. The failure mechanism of the TBCs during burner rig test (BRT) has been investigated via finite element modeling (FEM) and in-situ acoustic emission (AE) technique systematically. During the BRT, the oxygen-propane flame was heated onto the surface of the coating samples with the dwell time 3 min, then the surface and the backside of the coating samples were cooled by the compressed air simultaneously for 3 min. This can be viewed as one thermal cycle. Then repeat the same heating and cooling process. The history and distribution of the temperature along the through-thickness direction of the coating samples has been obtained via FEM, and the residual stress at different stages has been also calculated. The FEM results have indicated that large tensile stress and compressive stress existed at the heating stage and cooling stage of each thermal cycle, respectively. The crack propagation tends to occur at the initial period of heating stage in the BRT process. The in-situ acquisition of the AE signals during the BRT has also been adopted. The crack propagation patterns have been obtained based on the analysis of AE signals. The filtering technique has been used to exclude the disturbance of the noise in the process of BRT in order to capture the actual and effective AE signals which represent the crack propagation and the deformation of the coating systems. Based on the characteristic waveform of effective AE signals, the Fast Fourier Transformation (FFT) and wavelet transformation has been adopted to analyze the key distribution range of the amplitude and frequency. The investigation results indicate that the acquired AE signals during BRT mainly include signals which came from the plastic deformation of the substrate and creep of each layers, propagation of the vertical crack and propagation of the interfacial cracks (horizontal crack). The detailed failure mechanisms of the TBCs during BRT have been clarified in the current work.

Relationship Between Lamellar Structure and Elastic Modulus of Thermally Sprayed Thermal Barrier Coatings with Intra-splat Cracks

Atmospheric plasma sprayed thick thermal barrier coatings: Microstructure, thermal shock behaviors and failure mechanism

Effect of porous microstructure on the elastic modulus of plasma-sprayed thermal barrier coatings: Experiment and numerical analysis

Shakedown Analysis and Experimental Study of Thermal Barrier Coatings

Effect of Top-Coat Thickness and Interface Fluctuation on the Residual Stress in APS-TBCs

Prediction of critical rupture of plasma-sprayed yttria stabilized zirconia thermal barrier coatings under burner rig test via finite element simulation and in-situ acoustic emission technique

SEM-Guided Finite Element Simulation of Thermal Stresses in Multilayered Suspension Plasma-Sprayed TBCs

Structural Optimization for the Thermal Conductivity and Thermal Cycling Behavior in Thermal Barrier Coatings and Analysis of Thermomechanical Properties by Computational Investigation

Investigating the Cmas Corrosion Resistance and Thermal Cycling Failure Behavior of Porous Thermal Barrier Coatings with Different Morphologies Prepared by Plasma Spraying

Simulation of Residual Stresses and Their Effects on Thermal Barrier Coating Systems Using Finite Element Method

A Simulation Study on the Crack Propagation Behavior of Nanostructured Thermal Barrier Coatings with Tailored Microstructure

Thermal Conductivity Prediction in Air Plasma Sprayed Thermal Barrier Coatings Containing Multifarious Defects

Thermal shock resistance and failure analysis of La2(Zr0.75Ce0.25)2O7-based TBCs produced by atmospheric plasma spraying

Modeling 3D TGO dynamic growth and stresses and the resulting modes of buckling failure in thermal barrier coatings

Determination and Analysis of Crack Growth Resistance in Plasma-Sprayed Thermal Barrier Coatings

Effect of spraying ceramic powder pore structure on thermophysical properties of plasma-sprayed thermal barrier coatings

Thermal Stability of Plasma-Sprayed Thick Thermal Barrier Coatings Using Triplex ProTM-200 Torch

Damage Grading Evaluation of Thermal Barrier Coatings under CMAS Corrosion

Mechanisms of crack healing in dense Yb-Si-O environmental barrier coatings by plasma spray-physical vapor deposition

Failure behaviour of EB-PVD YSZ thermal barrier coatings under simulated aero-engine operating conditions

Growth selection induced residual stresses and fracture behavior of as‐deposited thermal barrier coatings