Abstract:Environmental barrier coatings (EBCs) are increasingly being used in the high-temperature sections of gas turbines because of their protective effects on SiC fiber-reinforced SiC ceramic matrix composites (SiCf/SiC CMCs) when subjected to high-temperature water oxygen corrosion. The objective of this study was to investigate the failure behavior of EBCs prepared on SiCf/SiC CMC matrix materials under coupled high-temperature and load conditions. A plasma spray-physical vapor deposition (PS-PVD) method was used to prepare Si/3Al2O3·2SiO2/Yb2SiO5 EBC composite coatings on the surface of SiCf/SiC ceramic matrix composites. In situ scanning electron microscopy was used to study the evolutionary behavior of the coating surface cracks at different temperatures and the failure and fracture mechanism of the coating/substrate when held at 766 °C and subjected to different loading conditions. The results show that no significant crack extension occurred on the coating surface as the temperature of the coated specimen increased from room temperature to 766 °C in the absence of an applied tensile load, indicating that the effect of a single temperature factor on the failure of the specimen was negligible. However, under coupled high-temperature and load conditions, the specimens fractured at a load of 340 N when subjected to 766 °C, indicating that the coated sample is more likely to fail when subjected to high-temperature and tensile loading. The step-like fracture exhibits features consistent with the coating fracture and spalling caused by surface cracks extending from the coating surface to the interior. The spalling, large crack formation and step-like shape of the fracture in the coating and the substrate indicate that cracks were generated between the coating and the substrate under the coupled high-temperature and load conditions. The generation and extension of cracks in both parts eventually led to full specimen rupture.

Mechanisms of crack healing in dense Yb-Si-O environmental barrier coatings by plasma spray-physical vapor deposition

Mechanism of vertical crack formation in Yb2SiO5 coatings deposited via plasma spray-physical vapor deposition

Constrained Healing and Morphology Change Mechanism of 2D Cracks in Plasma Sprayed Thermal Barrier Coatings

In Situ High-Temperature Tensile Fracture Mechanism of PS-PVD EBCs

Undulating and Porous Structure Tuned Surface Cracking Behavior of Yb2Si2O7 Environmental Barrier Coatings Under Steam Cycling

Improvement in the Self-healing Property of Plasma-Sprayed Environmental Barrier Coatings by SiC Addition

Crack-healing behaviour of MoSi2 dispersed Yb2Si2O7 environmental barrier coatings

The Crack Behavior and Delamination Mechanisms of Air Plasma Sprayed Thermal Barrier Coatings under Ultrasonic Plasma Jet at 1600 °C

High-temperature Oxidation Behavior and Mechanical Properties of PS-PVD Sprayed Yb2Si2O7 Environmental Barrier Coatings

Influence of Spraying Power on Microstructure, Phase Composition and Nanomechanical Properties of Plasma-Sprayed Nanostructured Yb-silicate Environmental Barrier Coatings

Densification method of air-plasma-sprayed environmental barrier coatings achieved by pre-heat treatment

Characterization of Yb2SiO5-based environmental barrier coating prepared by plasma spray–physical vapor deposition

Exploring the Crack Propagation Behavior in Suspension Plasma Sprayed Thermal Barrier Coatings: an In-Situ Three-point Bending Study in Scanning Electron Microscope

In Situ Monitoring of Cracking Mechanisms in Multi-Layered Suspension Plasma-Sprayed Thermal Barrier Coatings

SiC modified self‐healing ytterbium disilicate materials for potential environmental barrier coating application

Unraveling the Cracking Mechanisms of Air Plasma-Sprayed Thermal Barrier Coatings: an In-Situ SEM Investigation

Rear Earth Oxide Multilayer Deposited by Plasma Spray-Physical Vapor Deposition for Envisaged Application as Thermal/Environmental Barrier Coating

Microstructure and Phase Composition Evolution of Dual-Phase Ytterbium Silicate Coatings Plasma Sprayed from Stoichiometric Yb2Si2O7 Feedstock Powder

Comprehensive understanding of coupled stress characteristics in ytterbium disilicate environmental barrier coatings undergoing corrosion transformation and thermal cycling

Structure, composition, and defect control during plasma spray deposition of ytterbium silicate coatings

Water Vapor Corrosion Behavior of Yb2SiO5 Environmental Barrier Coatings Prepared by Plasma Spray-Physical Vapor Deposition