Abstract:Environmental barrier coatings (EBCs) are increasingly being used in the high-temperature sections of gas turbines because of their protective effects on SiC fiber-reinforced SiC ceramic matrix composites (SiCf/SiC CMCs) when subjected to high-temperature water oxygen corrosion. The objective of this study was to investigate the failure behavior of EBCs prepared on SiCf/SiC CMC matrix materials under coupled high-temperature and load conditions. A plasma spray-physical vapor deposition (PS-PVD) method was used to prepare Si/3Al2O3·2SiO2/Yb2SiO5 EBC composite coatings on the surface of SiCf/SiC ceramic matrix composites. In situ scanning electron microscopy was used to study the evolutionary behavior of the coating surface cracks at different temperatures and the failure and fracture mechanism of the coating/substrate when held at 766 °C and subjected to different loading conditions. The results show that no significant crack extension occurred on the coating surface as the temperature of the coated specimen increased from room temperature to 766 °C in the absence of an applied tensile load, indicating that the effect of a single temperature factor on the failure of the specimen was negligible. However, under coupled high-temperature and load conditions, the specimens fractured at a load of 340 N when subjected to 766 °C, indicating that the coated sample is more likely to fail when subjected to high-temperature and tensile loading. The step-like fracture exhibits features consistent with the coating fracture and spalling caused by surface cracks extending from the coating surface to the interior. The spalling, large crack formation and step-like shape of the fracture in the coating and the substrate indicate that cracks were generated between the coating and the substrate under the coupled high-temperature and load conditions. The generation and extension of cracks in both parts eventually led to full specimen rupture.

Undulating and Porous Structure Tuned Surface Cracking Behavior of Yb2Si2O7 Environmental Barrier Coatings Under Steam Cycling

Comprehensive understanding of coupled stress characteristics in ytterbium disilicate environmental barrier coatings undergoing corrosion transformation and thermal cycling

Corrosion behavior and mechanism of ytterbium silicates environmental barrier coatings to thermal cycling in water vapor

Thermochemical Stability of Yb 2 Si 2 O 7 Environmental Barrier Coatings During Thermal Cycling and Water Vapor Corrosion at 1350 °C

Water Vapor Corrosion Behavior of Yb2SiO5 Environmental Barrier Coatings Prepared by Plasma Spray-Physical Vapor Deposition

Mechanisms of crack healing in dense Yb-Si-O environmental barrier coatings by plasma spray-physical vapor deposition

Failure mechanism of ytterbium silicate/silicon bi-layer environmental barrier coatings on SiCf/SiC composites upon long-time water vapor and oxygen corrosion test

Thermal cycling and steam corrosion behavior of Yb3Al5O12‐based multilayered environmental barrier coatings for SiCf/SiC

SiC modified self‐healing ytterbium disilicate materials for potential environmental barrier coating application

Crack-healing behaviour of MoSi2 dispersed Yb2Si2O7 environmental barrier coatings

Steam Degradation of Ytterbium Disilicate Environmental Barrier Coatings: Effect of Composition, Microstructure and Temperature

Yb2SiO5-Yb2Si2O7 Gradient Environment Barrier Coating ： Rational Design and Corrosion Behavior in Water Vapor Environment at 1300 ℃

Failure Mechanism of EB-PVD Thermal Barrier Coatings under the Synergistic Effect of Thermal Shock and CMAS Corrosion

High-temperature Oxidation Behavior and Mechanical Properties of PS-PVD Sprayed Yb2Si2O7 Environmental Barrier Coatings

High temperature corrosion behavior and the inhibition of apatite formation evolving from corrosion of (Y1−Yb )2SiO5 in water vapor environment

Structure, composition, and defect control during plasma spray deposition of ytterbium silicate coatings

Improvement in the Self-healing Property of Plasma-Sprayed Environmental Barrier Coatings by SiC Addition

Damage Tolerance and Extensive Plastic Deformation of β‐Yb2Si2O7 from Room to High Temperatures

Corrosion behavior of PS-PVD spray Yb2Si2O7 environmental barrier coatings during continuous water vapor exposure

In Situ High-Temperature Tensile Fracture Mechanism of PS-PVD EBCs

Mechanism of vertical crack formation in Yb2SiO5 coatings deposited via plasma spray-physical vapor deposition