Synthesis, crystal structure and properties of YB2C2
Yueming LiDepeng JiYiwang BaoJixin ChenHui ZhangGuorui Zhaoa School of Materials Science and Engineering,Dongguan University of Technology,Dongguan,Chinab Department of two-dimensional materials,Songshan Lake Materials Laboratory,Dongguan,Chinac State Key Laboratory for Green Building Materials,China Building Materials Academy,Beijing,Chinad Shenyang National Laboratory for Materials Science,Institute of Metal Research,Chinese Academy of Sciences,Shenyang,Chinae Electron Microscopy Center,South China University of Technology,Guangzhou,Chinaf School of Emergent Soft Matter,South China University of Technology,Guangzhou,China
DOI: https://doi.org/10.1080/21870764.2024.2350830
2024-05-10
Journal of Asian Ceramic Societies
Abstract:YB 2 C 2 is a novel ultra-high temperature ceramic material with high damage tolerance. In this work, the synthesis mechanism, crystal structure, electronic structure, elastic properties and thermal shock resistance of YB 2 C 2 were systematically investigated through experiments and calculations. It was determined by differential scanning calorimetry with the heating rate of 10°C/min that YB 2 C 2 was formed by the reaction of YB 2 C and C at about 1202°C, and became the main phase at 1450°C. The space group of YB 2 C 2 was determined to be P 4/ mbm by X-ray diffraction, transmission electron microscopy, Rietveld refinement and first-principles calculations for the first time. The lattice constants are a = b = 0.5351 nm and c = 0.3561 nm. The atom positions are as follows: Y is located at 2a (0, 0, 0), B is located 4 h (0.133, 0.633, 0.5) and C is located at 4 h (0.662, 0.162, 0.5). The chemical bonding of YB 2 C 2 displayed sharp anisotropy, with strong B-C bond within the B 2 C 2 nets, and weak Y-B/Y-C bond between Y atom layers and B 2 C 2 nets. Additionally, YB 2 C 2 exhibited abnormal thermal shock resistance when the thermal shock temperature exceeded 800°C, with the residual flexural strength at 1300°C being more than 70% of the strength at room temperature.
materials science, ceramics