Synthesis and electrochemical performance of poly(vinylidene fluoride)/SiO2 hybrid membrane for lithium-ion batteries
Yang Xia,Jiaojiao Li,Hongjie Wang,Zhangjun Ye,Xiaozheng Zhou,Hui Huang,Yongping Gan,Chu Liang,Jun Zhang,Wenkui Zhang
DOI: https://doi.org/10.1007/s10008-018-4161-2
IF: 2.747
2018-11-26
Journal of Solid State Electrochemistry
Abstract:<h3 class="a-plus-plus">Abstract</h3> <p class="a-plus-plus">In this work, a series of rationally designed hybrid membranes composed of poly(vinylidene fluoride) (PVDF) as polymer matrix and silica nanoparticles (SiO<sub class="a-plus-plus">2</sub>) as inorganic fillers are prepared by combining slurry coating method and phase inversion method. The effects of the added SiO<sub class="a-plus-plus">2</sub> nanoparticles on the porosity, electrolyte wettability, thermal stability, and ionic conductivity of PVDF/SiO<sub class="a-plus-plus">2</sub> hybrid membranes are investigated systematically. Compared to the commercial polypropylene (PP) membrane, PVDF/SiO<sub class="a-plus-plus">2</sub> hybrid membranes present enhanced physical and electrochemical performance. Particularly, the incorporation of 5 wt.% SiO<sub class="a-plus-plus">2</sub> to PVDF polymer matrix (PVDF5 hybrid membrane) shows the highest ionic conductivity of 1 × 10<sup class="a-plus-plus">−3</sup> S cm<sup class="a-plus-plus">−1</sup> at 25 °C among all the samples. The electrochemical tests demonstrate that the LiNi<sub class="a-plus-plus">0.8</sub>Co<sub class="a-plus-plus">0.1</sub>Mn<sub class="a-plus-plus">0.1</sub>O<sub class="a-plus-plus">2</sub>/Li coin cell assembled with PVDF5 hybrid membrane exhibits high reversible discharge capacity (179 mAh g<sup class="a-plus-plus">−1</sup> at 0.05 C), excellent cyclic stability (169 mAh g<sup class="a-plus-plus">−1</sup> after 100 cycles at 0.1 C), and superior rate performance, which are much better than other counterparts and PP separator. Moreover, as for the large capacity battery application, 1.1 Ah LiNi<sub class="a-plus-plus">0.8</sub>Co<sub class="a-plus-plus">0.1</sub>Mn<sub class="a-plus-plus">0.1</sub>O<sub class="a-plus-plus">2</sub>/graphite pouch cell with PVDF5 hybrid membrane can deliver a high discharge capacity of 992 mAh and good Coulombic efficiency of 99.5%. Evidently, the optimized PVDF/SiO<sub class="a-plus-plus">2</sub> hybrid membrane will be a very promising alternative to the commercial PP separator for advanced lithium-ion batteries.</p>
electrochemistry