Abstract:Abstract Central cracking refers to the formation of internal cavities in cross wedge rolling (CWR) products. It occurs in various materials such as aluminium/titanium alloys, steels and plasticine at room or elevated temperatures, driven by different central cracking mechanisms. However, these mechanisms are still elusive, and a unified central cracking predictive model is absent due to the complex stress states within the workpiece, including triaxial stress states, cyclic loading and severe shear effects. In this study, the underlying fracture mechanisms were revealed, and a robust unified damage model with sound physical meanings was developed using a lab-scale CWR physical model and finite element models. The physical model with the plasticine billets was built, allowing the CWR dies with different geometries rapidly 3D printed and the billets with various ductility efficiently manufactured. The central cracking transiting from brittle to ductile fracture was experimentally observed for the first time using specifically designed plasticine/flour composite samples at varying ductility. The corresponding physics-based central cracking predictive model was proposed and validated quantitatively with 60 groups of CWR tests and compared with ten existing damage models/fracture criteria. This study effectively solves the long-lasting central cracking problem in the CWR industry and enhances the scientific understanding of fracture mechanics in complex engineering applications.

Investigation of Closure of Internal Cracks During Rolling by FE Model Considering Crack Surface Roughness

Thermal-Mechanical Finite Element Analysis of Evolution of Surface Cracks During Slab Rolling

Evolution of Surface Crack on Slab During Rough Rolling Using Thermal-Mechanical FEM

Study on Measurement Method of Interior Stress Distributions in Engineering Rolled-Plates

Behaviour of longitudinal cracks on slab surfaces in V-H rolling processes

Research on the Behavior of Transversal Crack in Slab V–H Rolling Process by FEM

Crystallographic Study of Surface Finish in Pack Rolling of Thin Sheets

The Cracks on Slab Corner During Hot Rolling Process

Evolution of subsurface blisters and initiation of surface crack on slab during hot rolling using FEM

Research on Behavior of Slab Surface Defects in Forward Slip Zone during V-H Rolling Process

Analysis of Internal Crack Healing Mechanism under Rolling Deformation

Research on Crack Healing in Slab During Hot Rolling

Analysis of Crack Tip Stress of Transversal Crack on Slab Corner During Vertical-Horizontal Rolling Process by FEM

Behavior of Transversal Crack on Slab Corner During V-H Rolling Process

Closure Behavior of Spherical Void in Slab During Hot Rolling Process

Occurrence of Surface Defects on Strips During Hot Rolling Process by FEM

Phenomenological Anisotropic Study of Surface Finish in Pack Rolling

Effect of Rolling on Crack Behavior of FeCrAl Alloys in Ultra-Long Life

Investigation and prediction of central cracking in cross wedge rolling

Experimental and FE analysis of void closure in hot rolling of stainless steel

Modeling and Evaluation of Damages in Bismuth-containing Stainless Steel Rolling