Abstract:Abstract Central cracking in cross-wedge-rolled workpieces results in high wastage and economic loss. Recent cross-wedge rolling tests on two batches of steel showed that one batch formed central cracks, while the other was crack-free. The batches were both nominally of the same chemical composition and thermomechanical treatment history. In addition, both batches had passed all the standard quality assessments set for conventional forging processes. It was suspected that the different cracking behaviours were due to differences in microstructure between the two as-received steel billets, and the material in cross-wedge rolling (CWR) was more sensitive to the initial microstructure compared with other forging processes due to its specific loading condition including ostensibly compression and large plastic strain. Nevertheless, no previous study of this important problem could be identified. The aim of this study is, therefore, to identify the key microstructural features determining the central crack formation behaviour in CWR. The hot workability of the as-received billets was studied under uniaxial tensile conditions using a Gleeble 3800 test machine. Scanning electron microscope with energy-dispersive X-ray spectroscopy and electron backscatter diffraction was applied to characterise, quantitatively analyse, and compare the chemical composition, phase, grain, and inclusions in these two billets, both at room temperature and also at the CWR temperature (1080 °C). Non-metallic inclusions (oxides, sulphides, and silicates) in the billets were determined to be the main cause of the reported central cracking problem. The ductility of the steels at both room and elevated temperatures deteriorated markedly in the presence of the large volumes of inclusions. Grain boundary embrittlement occurred at the CWR temperature due to the aggregation of inclusions along the grain boundaries. It is suggested that a standard on specifying the inclusion quantity and size in CWR billets be established to produce crack-free products.

Research on Crack Healing in Slab During Hot Rolling

The Cracks on Slab Corner During Hot Rolling Process

Evolution of Surface Crack on Slab During Rough Rolling Using Thermal-Mechanical FEM

The Causes and Control of Longitudinal Edge Cracks of the Plate

Microstructure and mechanical properties of internal crack healing in a low carbon steel

Effect of Rolling Process Parameters on Transverse Cracks on the Surface of Q345 Steel

Restoration of Impact Properties of Internal Crack Healing in A Low Carbon Steel

Crack Healing And Mechanical Properties Recovery In Sa 508-3 Steel

Analysis of Internal Cracks in Continuous Casting Slabs with Soft Reduction

Effect of Heat Treatment on Microstructure and Hardness of Internal Crack Healing in a Low Carbon Steel

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Microstructural effects on central crack formation in hot cross-wedge-rolled high-strength steel parts

Hot Cracking of Low Alloy Steels in Simulated Continuous Casting-Direct Rolling Process

Investigation of the Influence of Deep Rolling on the Thermal Fatigue Cracking for Aisi H13 Steel

The Effects of Homogenizing and Quenching and Tempering Treatments on Crack Healing

Establishment of Thermal Ductile Fracture Criterion for As-Cast 42CrMo Steel and Its Application in Hot Ring Rolling Process

Effect of deformation modes and heat treatment on microstructure and impact property restoration of internal crack healing in SA 508 steel

Investigation and prediction of central cracking in cross wedge rolling

Evolution Behaviors and Mechanisms of Internal Crack Healing in Steels at Elevated Temperatures

Numerical Simulation Research and Application of Convex Roll for Efficient Soft Reduction of Continuous Casting Slab

Reason for Edge Cracking of Cold-Rolled 55Mn Strip Steel and the Cold-rolling Control Measures