Si 3 N 4 -doped Zr 50 Al 15 Ni 10 Cu 25 glassy alloy by mechanical alloying and sintering process

Xue-qiong Ouyang,Wo-yun Long,Jian-ze Bian,Chao Gao,An-xian Lu

DOI: https://doi.org/10.1007/s11771-010-0606-1

2010-01-01

Journal of Central South University of Technology

Abstract:Zr 50 Al 15 Ni 10 Cu 25 amorphous powder was synthesized by mechanical alloying. The effect of Si 3 N 4 addition on the crystallization behavior of the alloy during sintering process was studied. Thermal stability of the powders was performed by differential scanning calorimetry (DSC). The phase and microstructure of the powders and bulk specimens sintered were determined by X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The results show that, introducing 0.05% (mass fraction) Si 3 N 4 can enhance the crystallization activation energy of the Zr 50 Al 15 Ni 10 Cu 25 amorphous powders, which indicates that Si 3 N 4 addition has hindrance effect on forming crystals from Zr 50 Al 15 Ni 10 Cu 25 amorphous powder. However, 0.10% Si 3 N 4 results in the decrease of the crystallization activation energy, which makes its crystallization process easy to occur.