Formation and Compressive Properties of A Ni-Ti-Zr-Al-Cu-Si Amorphous Alloy

Liang Weizhong,Ning Zhiliang,Sun Jianfei,Shen Jun

DOI: https://doi.org/10.3321/j.issn:1002-185x.2006.09.023

2006-01-01

Rare Metal Materials and Engineering

Abstract:Formation of NiTiZrAlCuSi amorphous alloy was investigated by using differential scanning calorimetry (DSC), differential thermal analysis (DTA) and X-ray diffraction (XRD). When prepared by using the simple copper mould casting, the maximum diameter of glassy rods increased from < 0.5 mm for the Ni42Ti25Zr25Al8 alloy to 1 mm for the Ni42Ti20Zr25Al8Cu5 alloy and to 4 mm for the Ni42Ti20Zr21.5Al8Cu5Si3.5 alloy. The maximum reduced glass transition temperature T-rg(=T-g/T-l) of 0.570 and the maximum supercooled liquid region Delta H (=T-x-T-g) of 93 K were attained in Ni42Ti20Zr21.5Al8Cu5Si3.5 and Ni42Ti20Zr20.5Al8Cu5Si4.5 alloys, respectively. Addition of a proper amount of Si can effectively enhance the glass-forming ability by suppressing the formation of primary Ni(TiZr) and (TiZr)(CuAl)(2) phases. The compression test at room temperature showed that the Ni42Ti20Zr21.5Al8Cu5Si3.5 alloy has a high fracture strength of 2724 MPa.