Abstract:In preparing Cu2ZnSnSe4 (CZTSe) thin films, selenization at high Se pressure is likely to form a thick molybdenum diselenide (MoSe2) layer. An excessively thick MoSe2 layer degrades the performance of CZTSe solar cells. Annealing under low Se pressure has been suggested to prevent the formation of such a thick MoSe2 layer. However, the potential loss of Sn metal from CZTSe thin films at low Se pressure or high temperature raises the additional difficulty of controlling the compositions and phases of the films. Carefully controlling these selenization parameters to yield high-quality CZTSe thin films is important. This study investigates the loss of Sn and the formation of molybdenum diselenide in CZTSe thin films at low Se pressure. Three-step selenization at low Se pressure is performed on an electrodeposited Cu/Sn/Zn precursor to prepare high-quality CZTSe thin films. In the first step, rapid thermal annealing with a substrate temperature of 500°C and a low Se vapor pressure of 4.6Pa was performed to reduce the loss of Sn and the thickness of the MoSe2 layer, and thus to obtain a Cu-poor and Zn-rich film. In the second step, a high annealing temperature of 570°C and an inert gas at high pressure was used to improve elemental diffusion and increase the uniformity of the elemental distribution. In the third step, thermal annealing with a substrate temperature of 500°C and a low Se vapor pressure of 4.6Pa was performed to reduce the loss of Sn and the thickness of the MoSe2 layer, and to eliminate the impurity phase of SnSe (which was formed in the second step of annealing) on the surface of the CZTS films. The loss of Sn and the formation of molybdenum diselenide in the CZTSe thin films are negligible when this three-step selenization at low Se pressure is used. When the selenization parameters are properly controlled, CZTSe solar cells with an efficiency of as high as 8.2% can be obtained.

Solution-processed highly efficient Cu2ZnSnSe4 thin film solar cells by dissolution of elemental Cu, Zn, Sn, and Se powders.

Novel solution processing of high-efficiency Earth-abundant Cu2 ZnSn(S,Se)4 solar cells.

Novel non-hydrazine solution processing of earth-abundant Cu2ZnSn(S,Se)4 absorbers for thin-film solar cells

A Non-Vacuum Solution Route to Prepare Amorphous Metal Oxides Thin Films for Cu2znsn(S,Se)(4) Solar Cells

Fabrication of a High-Quality Cu2ZnSn(S,Se)4 Absorber Layer Via an Aqueous Solution Process and Application in Solar Cells.

Uniform monolayer Cu2ZnSn(S,Se)4 film based on novel precursor solution

Solution-processed Cu 2 CdSn(S,Se) 4 thin film solar cells

Precursor Solution Chemistry Via Water Additive Enabling CZTSSe Solar Cells with over 12％Efficiency

A CZTSe Solar Cell with 8.2% Power Conversion Efficiency Fabricated Using Electrodeposited Cu/Sn/Zn Precursor and a Three-Step Selenization Process at Low Se Pressure

Fabrication of a Cu2ZnSn(S,Se)4 photovoltaic device by a low-toxicity ethanol solution process.

Cu2 ZnSn(S1-x Se x )4 thin film solar cells prepared by water-based solution process

Versatile and Low-Toxic Solution Approach to Binary, Ternary, and Quaternary Metal Sulfide Thin Films and Its Application in Cu 2 ZnSn(S,Se) 4 Solar Cells

Solution transformation of SnS into Cu2ZnSnS4xSe4(1-x) for solar water splitting

Eliminating Cracking Morphology of Solution-Processed CZTSSe Absorbers by Sn-rich Composition Engineering

Benign solution processed Cu2ZnSn(Se, S)4 photovoltaic

Above 10% efficient electrodeposited Cu2ZnSn(S,Se)4 solar cell achieved by modifying precursor

Improvement of grain growth and composition distribution of Cu2ZnSn(S,Se)4 by using chloride-based precursor solution

Electrochemical synthesis of Cu 2 ZnSnS 4 and Cu 2 ZnSnSe 4 thin films for solar cells

Benign Solutions and Innovative Sequential Annealing Processes for High Performance Cu2ZnSn(Se,S)4 Photovoltaics

Fabrication of Cu2ZnSn(S,Se)4 absorber films by selenization of different Cu2ZnSnS4 nanocrystal coatings

Cu2ZnSn(S,Se)4 Thin Film Solar Cells Fabricated with Benign Solvents