Abstract:The enhancement of charge separation and utilization efficiency in both the bulk phase and interface of semiconductor photocatalysts, as well as the expansion of light absorption range, are crucial research topics in the field of photocatalysis. To address this issue, twinned Cd0.5Zn0.5S (T-CZS) homojunctions consisting of wurtzite Cd0.5Zn0.5S (WZ-CZS) and zinc blende Cd0.5Zn0.5S (ZB-CZS) were synthesized via a hydrothermal method to facilitate the bulk-phase charge separation. Meanwhile, Cu2-xSe with localized surface plasmon resonance effect (LSPR) generated by Cu vacancies was also obtained through a hydrothermal process. Due to their opposite electronegativity, a solvent evaporation strategy was employed to combine Cu2-xSe and T-CZS by intermolecular electrostatic. After optimization, the photocatalytic hydrogen (H2) evolution rate of 5 wt% Cu2-xSe/T-CZS reached an impressive value of 60 mmol∙h-1∙g-1, which was 4.6 and 66.6 times higher than that of pure Cu2-xSe and T-CZS, respectively. Furthermore, this composites demonstrated a remarkable rate of 0.46 mmol∙h-1∙g-1 under near-infrared (NIR) wavelength (>800 nm). The enhanced performance observed in Cu2-xSe/T-CZS can be attributed to its unique and efficient double S-scheme charge transfer mechanism which effectively suppresses rapid recombination of electron-hole pairs both within the bulk phase and at the surface interfaces; this conclusion is supported by Density Functional Theory (DFT) calculations as well as electron paramagnetic resonance spectroscopy analysis. Moreover, incorporation of Cu2-xSe enables effective utilization ultraviolet visible-near infrared (UV-Vis-NIR) light by the composites while facilitating injection "hot electrons" into T-CZS for promoting photocatalytic reactions. This study provides a potential strategy for achieving efficient solar energy conversion through synergistic integration of non-stoichiometric plasmonic materials with photocatalysts with twinned-twinned structures.

Benign Solutions and Innovative Sequential Annealing Processes for High Performance Cu2ZnSn(Se,S)4 Photovoltaics

Benign solution processed Cu2ZnSn(Se, S)4 photovoltaic

Novel solution processing of high-efficiency Earth-abundant Cu2 ZnSn(S,Se)4 solar cells.

Non‐Hydrazine Solutions in Processing CuIn(S,Se)2 Photovoltaic Devices from Hydrazinium Precursors

Non-Hydrazine Solution Processed Culn(Se,S)(2) Photovoltaic Device

Solution transformation of SnS into Cu2ZnSnS4xSe4(1-x) for solar water splitting

: a promising approach for next generation thin fi lm photovoltaics

Exploring the optimal two-step selenization process to enhance the performance of ionic liquid solution based Cu2ZnSn(S,Se)4 thin film solar cells

CZTS nanocrystals: a promising approach for next generation thin film photovoltaics

Determining and Controlling the Stoichiometry of Cu2ZnSnS4 Photovoltaics: the Physics and Its Implications

Double S-scheme Cu2-xSe/twinned-Cd0.5Zn0.5S homo-heterojunctions with surface plasmon effects for efficient photocatalytic H2 evolution

Se as hetero-nucleation seeds reinforcing intermetallic diffusion for improved electrodeposition-processed CZTS solar cells

Improving the Performance of Solution-Based CZTSSe Absorber by Selenization Annealing with Selenium Powder in Argon

Achieving 11.95% Efficient Cu2ZnSnSe4 Solar Cells Fabricated by Sputtering a Cu-Zn-Sn-Se Quaternary Compound Target with a Selenization Process

Rational Defect Passivation of Cu2ZnSn(S,Se)4 Photovoltaics with Solution-Processed Cu2ZnSnS4:Na Nanocrystals.

Hydrazine Solution Processed Cusbse2: Temperature Dependent Phase and Crystal Orientation Evolution

Environmentally Friendly Synthesis of Copper Zinc Tin Sulfide (CZTS) Thin Film Solar Cells: Advancing Sustainable Photo-Energy Conversion with Low-Temperature Chemical Processing

Passivating SnZn Defect and Optimizing Energy Level Alignment via Organic Silicon Salt Incorporation toward Efficient Solution‐Processed CZTSSe Solar Cells

CZTSSe solar cell with an efficiency of 10.19% based on absorbers with homogeneous composition and structure using a novel two-step annealing process

Toward High Efficient Cu2 ZnSn(Sx ,Se1- x )4 Solar Cells: Break the Limitations of VOC and FF

Spatial Element Distribution Control in a Fully Solution-Processed Nanocrystals-Based 8.6% Cu 2 ZnSn(S,Se) 4 Device