Comparative analysis of the microstructures and mechanical properties of Co-Cr dental alloys fabricated by different methods
Yanan Zhou,Ning Li,Jiazhen Yan,Qiang Zeng
DOI: https://doi.org/10.1016/j.prosdent.2017.11.015
Abstract:Statement of problem: Limited information is available regarding the microstructures and mechanical properties of Co-Cr dental alloys prepared using conventional casting (CAST), computer numerical control (CNC) milling, and selective laser melting (SLM). Purpose: The purpose of this in vitro study was to evaluate the mechanical properties and microstructures of Co-Cr dental alloys fabricated using conventional casting, computer numerical control milling, and selective laser melting and to estimate the potential of applying the SLM technique in prosthetic dentistry. Material and methods: Each group (n=6) of 50-mm-long Co-Cr alloy, dumbbell-shaped specimens was fabricated using the CAST, CNC, and SLM techniques. For each technique, the corresponding commercial alloy material was used. The mechanical properties were evaluated using a tensile test according to International Organization for Standardization (ISO) standard 6892, including 0.2% yield strength, ultimate tensile strength, elongation, and fracture analysis. The microstructures of the specimens were evaluated by using metallurgical microscopy, X-ray diffraction (XRD), and scanning electron microscopy. The Tukey honest significant difference test (α=.05) was used to statistically analyze the 0.2% yield strength, ultimate tensile strength, and microhardness values. Results: The microstructures of the SLM specimens exhibited homogeneously distributed fine grains, dispersed second-phase particles, and few defects, and the XRD results showed the α-Co phase predominated, with minimal ε-Co phase and no harmful needle σ phase in the SLM group. The mean ±standard deviation of the 0.2% yield strength of the SLM specimens was 790 ±11 MPa, and the ultimate tensile strength was 1072 ±18 MPa. These values exceeded those of the CAST and CNC specimens by approximately 50% (P<.05). The SLM group showed the highest microhardness (475.3 ±10.2 HV10), followed by the CNC (325.2 ±17.8 HV10) and CAST group (323.7 ±27.2 HV10). Additionally, the ductility and toughness of the SLM specimens were also better than those of the other 2 groups. No significant differences were found in the mechanical performance between the CNC and CAST specimens (P>.05). Conclusions: The microstructures and mechanical properties of Co-Cr dental alloys were dependent on the fabrication techniques. The SLM specimens exhibited better microstructures and mechanical properties than those fabricated with CNC or CAST.