Ti-Ge binary alloy system developed as potential dental materials.

Wen-Jiao Lin,Ben-Li Wang,Ke-Jin Qiu,Fei-Yu Zhou,Li Li,Jun-Pin Lin,Yan-Bo Wang,Yu-Feng Zheng

DOI: https://doi.org/10.1002/jbm.b.32793

2012-01-01

Abstract:As-cast TixGe (x = 2, 5, 10, 20 wt %) binary alloys were produced in this work, and various experiments were carried out to investigate the microstructure, mechanical properties, in vitro electrochemical and immersion corrosion behaviors as well as cytotoxicity with as-cast pure Ti as control, aiming to study the feasibility of TixGe alloy system as potential dental materials. The microstructure of TixGe alloys changes from single a-Ti phase to a-Ti + Ti5Ge3 precipitation phase with the increase of Ge content. Mechanical tests show that Ti5Ge alloy has the best comprehensive mechanical properties. The corrosion behavior of TixGe alloys in artificial saliva with different NaF and lactic acid addition at 37 degrees C indicates that Ti2Ge and Ti5Ge alloys show better corrosion resistance to fluorine-containing solution. The cytotoxicity test indicates that TixGe alloy extracts show no obvious reduction of cell viability to L-929 fibroblasts and MG-63 osteosarcoma cells, similar to pure Ti which is generally acknowledged to be biocompatible. Considering all these results, Ti2Ge and Ti5Ge alloys possess the optimal comprehensive performance and might be used as potential dental materials. (c) 2012 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 2012.