Abstract:Two kinds of spherically hierarchical structures were fabricated and characterized in this paper. With rough surfaces of high spatial frequency superimposed on sphere surfaces of lower spatial frequency, the surface morphology of spherically hierarchical structures was simulated, and effects of characteristic parameters on the surface morphology were investigated. Au fiber of diameter Φ30μm was melted from one end for a specific length and cooled down naturally to form an Au microsphere with desirable diameter. ZnO nanowires were hydrothermally synthesized on Au and SiO2 microspheres respectively, producing two types of spherically hierarchical structures. Based on micrographs of scanning electron microscopy (SEM) and operators of filtration, line edge detection and fitting of MatLab software, roundness errors of Au and SiO2 microspheres as well as the surface morphology of corresponding spherically hierarchical structures were characterized. Roundness errors of Au microspheres with diameters Φ197μm and Φ244μm are 2.51μm and 4.08μm respectively, whilst that of SiO2 microspheres with diameters Φ44.5μm and Φ50.2μm are 0.88μm and 0.98μm respectively. Values of characteristic parameters of the surface morphology exhibited that non-Gaussian rough surfaces of spherically hierarchical structures were produced. Simulation results were compared with characterization ones, showing the former is in agreement with the latter. The results can be used to batch fabricate spherically hierarchical structures and to construct corresponding sensors in medicine, biology, electrochemistry, and environmental monitoring domains.

Construction of 3d Arrays of Cylindrically Hierarchical Structures with Zno Nanorods Hydrothermally Synthesized on Optical Fiber Cores

Preparation and Characterization of a ZnO Nanowires-based Cylindrical Hierarchical Structure

Multiple-Patterning Nanosphere Lithography for Fabricating Periodic Three-Dimensional Hierarchical Nanostructures.

Conversion of large-scale oriented ZnO rod array into nanotube array under hydrothermal etching condition via one-step synthesis approach

Simulation and ZnO Nanowires-Based Generation of a Hierarchical Structure on an Optical Fiber Core

Fabrication of Spherically Hierarchical Structures with ZnO Nanowires Synthesized on Au and SiO2 Microspheres

Effects of the Geometries of Micro-Scale Substrates on the Surface Morphologies of ZnO Nanorod-Based Hierarchical Structures

Hydrothermal Fabrication of Zno Nanorod-Based Grating Patterns with Arrays of Optical Fiber Cores As Templates

Architecting three-dimensional ZnO nanorods

Chemical Growth of Zno Nanorod Arrays on Textured Nanoparticle Nanoribbons and Its Second-Harmonic Generation Performance

Alignment-controlled Hydrothermal Growth of Well-Aligned ZnO Nanorod Arrays

Synthesis of bilayer ZnO nanowire arrays: Morphology evolution, optical properties and photocatalytic performance

Hydrothermal Synthesis of Well-Aligned ZnO Nanorod Arrays on Silicon

Electronic Structure and Optical Properties of Vertically Aligned Zno Nanorod Arrays Grown by Low-Temperature Hydrothermal Method

Hierarchical Assembly Of Zno Nanostructures On Sno2 Backbone Nanowires: Low-Temperature Hydrothermal Preparation And Optical Properties

Mechanical-Agitation-Assisted Growth of Large-Scale and Uniform ZnO Nanorod Arrays Within 3D Multichannel Monolithic Substrates

Large-area zinc oxide nanorod arrays templated by nanoimprint lithography: control of morphologies and optical properties

Fabrication of oriented ZnO nanorod arrays and their optical performances

Novel Single-Crystalline Hierarchical Structured Zno Nanorods Fabricated Via A Wet-Chemical Route: Combined High Gas Sensing Performance with Enhanced Optical Properties

Sunlight-assisted Fabrication of a Hierarchical ZnO Nanorod Array Structure

A simple route to scalable fabrication of perfectly ordered ZnO nanorod arrays