Abstract:Although 4Ce4YSZ has high corrosion resistance, it faces challenges concerning its sinterability and ionic conductivity. Therefore, we studied destabilization behavior caused by corrosion and oxygen vacancy ordering according to ZnO doping. Powders of (4Ce4YSZ)1−x(ZnO)x (x = 0.5, 1, 2, 4 mol%) were synthesized using the sol-gel method. With the addition of ZnO, the cubic phase increased, and secondary phases were not observed. The (111) peak showed a higher angle shift in ZnO-doped 4Ce4YSZ compared to 4Ce4YSZ, and TEM-SAED revealed a reduction in the spacing of the (011)t plane, suggesting lattice contraction due to the substitution of the smaller Zn2+ (60 Å) for Zr4+ (84 Å) in the lattice. The local atomic structure analysis was conducted using EXAFS to investigate the oxygen vacancy ordering behavior. Zr K-edge Fourier transform data revealed a decrease in the Zr-O1 peak intensity with an increasing amount of ZnO doping, indicating an increase in oxygen vacancies. The Zr-O1 peak position shifted to the right, leading to an increase in the Zr-O1 interatomic distance. In the Y K-edge Fourier transform data, the Y-O1 peak intensity did not decrease, and there was little variation in the Y-O1 interatomic distance. These results suggest that the oxygen vacancies formed due to ZnO doping are located in the neighboring oxygen shell of Zn, rather than in the neighboring oxygen shells of Y and Zr. Impedance measurements were conducted to measure the conductivity, and as the amount of ZnO doping increased, the total conductivity increased, while the activation energy decreased. The increase in oxygen vacancies by ZnO doping contributed to the enhancement of conductivity, and it is considered that these created oxygen vacancies did not interact with Zn2+ and did not form defect associations. Fluoride-based molten salts were introduced to the specimens to assess the corrosion behavior in a molten salt environment. Yttrium depletion layers (YDLs) were formed on the surfaces of all specimens due to the leaching of yttrium. However, Ce remained relatively stable at the interface according to EDS line scans, suggesting a reduction in the phase transformation (cubic, tetragonal to monoclinic) typically associated with yttrium leaching in YSZ.

Degradation of CeO2 and TiO2 co-stabilized ZrO2 by the V2O5 molten salts and Na2SO4 + V2O5 molten salts

Hot corrosion behaviors of SrZrO3 ceramic co-doped with Y2O3 and Yb2O3 in molten Na2SO4, V2O5, and Na2SO4 + V2O5 salts mixture

Improving the Comprehensive Properties of ZrO2–C Materials with Aid of TiO2 Addition

Phase Stability and Slag-Induced Destabilization in MnO2 and CeO2-Doped Calcia-Stabilized Zirconia

Phase evolution and hot corrosion behavior of Yb2O3 and CeO2 co-doping YSZ ceramics under high temperature

TBCs materials of Lu2O3/TiO2/ Nb2O5 codoped ZrO2

Oxygen Vacancy Ordering and Molten Salt Corrosion Behavior of ZnO-Doped CeYSZ for Solid Oxide Membranes

Comparison of corrosion behaviors of Sc2O3-CeO2 co-stabilized ZrO2 and YSZ ceramics exposed to CMAS at 1250°C

Research on the Existence and Stability of Interfacial Tetragonal Zirconia Formed on Zirconium Alloys

Phase stability, thermophysical properties, thermal shock behavior and CMAS resistance of Sc2O3-CeO2 co-stabilized ZrO2 TBCs

Phase stability and hot corrosion behavior of ZrO2–Ta2O5 compound in Na2SO4–V2O5 mixtures at elevated temperatures

The Study on Degradation of Y<sub>2</sub>O<sub>3</sub>-CeO<sub>2</sub>-Partially Stabilized ZrO<sub>2</sub> Adding Al<sub>2</sub>O<sub>3</sub> Particles at Low Temperature

Effect of Mass Fraction of CeO2 on Structure of Zirconolite-based Glass-ceramics

Hot-Corrosion Behavior of Gd2O3–Yb2O3 Co-Doped YSZ Thermal Barrier Coatings in the Presence of V2O5 Molten Salt

Hot corrosion resistance of oxide‐doped yttria‐stabilized zirconia powder in V2O5 molten salt

Immobilization Behavior of Cerium Ions in the Zirconolite Ceramic Solidified Radioactive Waste Forms

Thermal and mechanical properties of Sc2O3–CeO2 co-stabilized zirconia ceramic as promising thermal barrier coating material

Hot corrosion behavior of YSZ/ZrW2O8 composites exposed to V2O5 at 700 °C and 850 °C in air

Degradation mechanism of dual-phase thermal barrier coatings Gd2Zr2O7 + 8YSZ under hot corrosion in pure Na2SO4

Effect of Al2O3 on the Phase Stability of Y-Ce-TZP/Al2O3 Composites at Low Temperature

Phase and microstructure evolution of 0.2Zr1-Ce O2/Zr1-Ce SiO4 (0 ≤ x + y ≤ 1) ceramics designed to immobilize tetravalent actinides