Abstract:NbMoTaW and VCrTaW high-entropy alloys (HEA) coatings with near-equal atomic ratios were deposited onto the T91 substrate by magnetron sputtering. The two HEA coatings and the T91 substrate were irradiated to the peak damage 50 displacements per atom (dpa) and 100 dpa using 2.7 MeV Si2+ at 550 °C. X-ray diffraction (XRD), Scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive X-ray spectroscopy (EDS) and nanoindentation techniques were used to study the changes in grain morphology, microstructure, element distribution and hardness before and after irradiation. The results showed that the grain structure was stable and the coatings were closely bonded to the substrate after irradiation. The elements (Ta and W) near the grain boundary in NbMoTaW coating were depleted before irradiation, but they became homogenized after irradiation. A large number of dislocation loops were observed in both the T91 substrate and HEA coatings after irradiation, the HEA coatings significantly increased the doses required for the full evolution of the dislocation loops. With the increase of damage doses, the dislocation loops size of HEA coatings increased and the number density decreased. The size of the dislocation loops of the two coatings was similar, while the number density of the dislocation loops of NbMoTaW coating was lower than that of VCrTaW coating. Both HEA coatings were significantly hardened after irradiation and the hardening rate of NbMoTaW coating was lower than that of VCrTaW coating. Interestingly, the hardening rate of 50 dpa was higher than 100 dpa for both HEA coatings, which was determined by softening factor and hardening factor in the irradiation process. Based on the defects and hardening rate caused by irradiation, it was preliminarily concluded that NbMoTaW coating had better irradiation resistance, and the above results provide an important reference for the subsequent optimization of lead-based fast reactors structural materials.

Microstructural damage evolution of (WTiVNbTa)C5 high-entropy carbide ceramics induced by self-ions irradiation

Effect of High Temperature Annealing on the Microstructure and Thermal Shock Resistance of Tungsten Coatings Grown by Chemical Vapor Deposition

Irradiation damage in (Zr0.25Ta0.25Nb0.25Ti0.25)C high-entropy carbide ceramics

The Microstructural and Hardness Changes of Tungsten Fiber after Au2+ Irradiation

Microstructural Evolution in W-1%TiC Alloy Irradiated He Ions at High Temperatures

A Study on He Ion Irradiation Damage in (ti0.25zr0.25nb0.25ta0.25)c High-Entropy Carbide Ceramics from Room Temperature to 700 °C

Microstructure Evolution and Effect on Deuterium Retention in TiC- and ZrC-Doped Tungsten under He+ Ion Irradiation

Microstructure Evolutions of the W–TiC Composite Conducted by Dual-Effects from Thermal Shock and He-ion Irradiation

Microstructure and Hardening Effect of Pure Tungsten and ZrO2 Strengthened Tungsten under Carbon Ion Irradiation at 700°C

Effect of annealing on the microstructure behavior of D+-irradiated W-2vol.%TiC composite prepared by wet-chemical method

High Temperature Effects on Irradiation Damage of Ti2AlC

Microstructural changes induced in advanced tungsten grades under high temperature neutron irradiation

Microstructural changes in He-irradiated V-Cr-Ti alloys with low Ti addition at 700 °C

Microstructural Evolution and Mechanical Properties in Cu48Zr48Al4 Bulk Metallic Glass Composites Induced by He+ Ion Irradiation

Microstructural evolution in pure and ZrC strengthened tungsten under ion irradiation at 600°C

Irradiation Hardening and Microstructure Study of MAX-Phase-Dispersion-Strengthened Vanadium Alloy under Self-Ion Irradiation

Mechanical Properties and Microstructural Change of W–Y 2 O 3 Alloy under Helium Irradiation

Microstructure Evolution of Nonstoichiometric ZrC0.6 with Ordered Carbon Vacancies under Ion Irradiation

Thermal Effects in Ion Irradiated Ti2AlC and Ti3SiC2

The Structural Transitions of Ti3AlC2 Induced by Ion Irradiation

Dislocation loops, segregation and hardening induced by high-dose ion irradiation of NbMoTaW and VCrTaW high-entropy alloy coatings on the T91 substrate