Abstract:Phosphors with the compositions of x% Eu2O3-doped SrAl2O4 (x = 0.25, 0.5, 0.75, and 1.0, in mole ratio) were synthesized in air using solid state reaction method. From the SEM observations, we had found that the nano-cotton-filament-structured crystals were formed on the particle surfaces of all synthesized x% Eu2O3-doped SrAl2O4 powders, and their volume decreased with raising synthesis temperature. XRD patterns, TEM observations, and EDS analyses were used to analyze and confirm the compositions of the formed nano-cotton-filament-structured crystals, and the reaction sequences of Eu2O3-doped SrAl2O4 were well presented and proven in this study. When 260–265 nm were used as excitation wavelength, all the synthesized x% Eu2O3-doped SrAl2O4 phosphors would show photoluminescence emission intensity at three emission peaks with wavelengths of 590–592, 610–612, and 658 nm, which are respective corresponding to 5D0 → 7F1, 5D0 → 7F2, and 5D0 → 7F3 transitions of Eu3+ ions. The emission intensities of those characteristic peaks were apparently affected by the Eu2O3 concentration and synthesis temperature, and the concentration quench effect was also observed. The dominated emission light of all x% Eu2O3-doped SrAl2O4 phosphors was the transition of 5D0 → 7F1 (590–592 nm) peak, which was different from before research, and we would well discuss and explain the reason to cause this result.

The Effects of Fluxes on Aln:Eu2+ Blue Phosphors Synthesized by A Carbothermal Reduction Method

Synthesis of Eu2+‐Doped AlN Phosphors by Carbothermal Reduction

Improved Blue‐Emitting AlN:Eu2+ Phosphors by Alloying with GaN

Effect of Flux on the Composition and Luminescent Properties of Ca 0.68 Mg 0.2 SiO 3 :0.12Eu 3+ Red Phosphor

Effective Suppression of AlN Impurity in Synthesis of CaAlSiN 3 :Eu 2+ Phosphors under Condition of Atmospheric Pressure

Synthesis and Photoluminescence of Eu, Mg-alon Phosphors by Carbothermal Reduction

Preparation of Eu2+-doped AlN Phosphors by Plasma Activated Sintering

Carbothermal Synthesis of CaAlSiN3:Eu2+ Red-Emitting Phosphors and the Photoluminescent Properties

Synthesis, structure, and luminescence properties of SrSiAl<sub>2</sub>O<sub>3</sub>N<sub>2</sub>:Eu<sup>2+</sup> phosphors for light-emitting devices and field emission displays

Synthesis of CaAlSiN3:Eu2+ Nitride Phosphors from Entire Oxides Raw Materials and Their Photoluminescent Properties

Atmospheric Pressure Preparation of Red-Emitting Caalsin3:Eu2+ Phosphors with Variable Fluxes and Their Photoluminescence Properties

Effect of Starting Composition and Post-Anneal on the Structure and Luminescence Properties of Eu-doped Ca-α-SiAlON Phosphors Prepared by Combustion Synthesis

Effects of synthesis temperature and Eu2O3 concentration on the crystalline phases and photoluminescence properties of SrAl2O4 phosphors

Luminescence of Ba 0.85 MgAl 10 O 16.94 :Eu 2+ 0.09 with Different Fluxes

Photoluminescence Properties of BaMgAl10O17:Eu2+ Phosphor Prepared by the Flux Method

Preparation and Luminescent Properties of SrAl2O4:Eu2+, Dy3+ Phosphor Via a Flux-Coprecipitation Method

Influence of Li2CO2-NaCl Flux on Synthesis of (Y,Gd)BO3:Eu

Intense Red Emission from Sr4Nb2O9:Eu3+ Phosphor by Introducing with SrF2 As Flux and Charge Compensator

Effect of Comburent Ratios on Combustion Synthesis of Eu-doped Β-Sialon Green Phosphors

Luminescence of Ba0.85MgAl10O16.94:Eu 0.09 2+ with different fluxes

Preparation of Sr1−xCaxLiAl3N4:Eu2+ Solid Solutions and Their Photoluminescence Properties