Abstract:A solid-state reaction method was used to synthesize Ca2+x MgSi2Eu0.025O7+x (x = 0-1.0) powders in the air atmosphere and in a reduction atmosphere (95% N2 + 5% H2) at 1350 °C and 4 h, and the reduction atmosphere was removed at 800 °C. Only the Ca2MgSi2O7 phase was found in the XRD pattern of the synthesized Ca2MgSi2Eu0.025O7 powder. The first important discovery was that when the x value of Ca2+x MgSi2Eu0.025O7+x powders was increased from 0.2 to 0.8, both Ca2MgSi2O7 and Ca3MgSi2O8 phases coexisted in the synthesized Ca2+x MgSi2Eu0.025O7+x powders, and the diffraction intensity of the Ca2MgSi2O7 (Ca3MgSi2O8) phase decreased (increased) with the x value. The second important discovery was that the Ca2MgSi2Eu0.025O7 phosphor exhibited stronger photoluminescence excitation (PLE), photoluminescence (PL), and decay curve properties than the Ca2.2MgSi2Eu0.025O7.2 phosphor, and the Ca3MgSi2Eu0.025O8 phosphor exhibited stronger PLE, PL, and decay curve properties than the Ca2+x MgSi2Eu0.025O7+x phosphors for x = 0.4, 0.6, and 0.8. For x = 0.2-0.8, the PL spectra of the Ca2+x MgSi2Eu0.025O7+x phosphors were a combination of the PL spectra of Ca2MgSi2Eu0.025O7 and Ca3MgSi2Eu0.025O8 phosphors. The third important discovery was that as the x value was increased, the maximum emission peak wavelengths of the Ca2+x MgSi2Eu0.025O7+x phosphors shifted to a lower value, the maximum emission intensity of the PL spectra increased, and the emission light changed from green and cyan to blue.

Effect of Flux on the Composition and Luminescent Properties of Ca 0.68 Mg 0.2 SiO 3 :0.12Eu 3+ Red Phosphor

Ca(La1-xEux)4Si3O13 red emitting phosphor for white light emitting diodes

Luminescence Properties of Ca2si5n8:Eu2+ Prepared by Gas-Pressed Sintering Using Baf2 As Flux and Cation Substitution

Effects of Composition Variations on the Crystalline Phases and Photoluminescence Properties of Ca 2+ x MgSi 2 Eu 0.025 O 7+ x Phosphors

Novel Optical Characteristics of Eu2+doped and Eu2+, Ce3+co-doped LiSi2N3phosphors by Gas-Pressed Sintering

Eu3+ Doped Ca3LiSbO6 and Eu3+, Li+ Co-Doped Ca3LiSbO6 Phosphors for White Light-Emitting Diodes

Intense Red Emission from Sr4Nb2O9:Eu3+ Phosphor by Introducing with SrF2 As Flux and Charge Compensator

Effect of Flux and Co-doping on Photoluminescence Properties of Zn2SiO4:Eu3+ Red Phosphors for Blue LED Excitable White LED Applications

Methods to Improve the Fluorescence Intensity of CaS:Eu2+ Red-Emitting Phosphor for White LED

The Effect of Eu2+ Doping Concentration on Luminescence Properties of Ca2-xMgSi2O7∶x Eu2+ Green Phosphor

Atmospheric Pressure Preparation of Red-Emitting Caalsin3:Eu2+ Phosphors with Variable Fluxes and Their Photoluminescence Properties

MgAl2O4:Mn2+ Red-Emitting Phosphor: Influence of MgF2 Flux on the Microstructure and Luminescence Properties

A Novel Li1/3Sr1/3Eu1/3MoO4 Red Phosphor: Influences of Sintering Temperature on Microstructures and Luminescent Properties

Effect of Li+ and Er3+ Co-Doping on the Luminescence Properties of Ba2sio4:Eu

Study on the Preparation of Red Phosphor CaO:Eu3+,Na+ by High Solid-state Method

Europium-Doped Calcium Silicate Nanoparticles as High-Quantum-Yield Red-Emitting Phosphors

Effect of the Proportion of Comburents and Eu2+ on Combustion Synthesis of Eu Doped Ca alpha SiAlON Phosphors

Luminescence properties of CaSi2O2N2 ∶Ce3+/Eu phosphors

Enhancement of luminescence properties of Ca2Al2SiO7: Eu3+ red phosphors by Li+, Na+, K+, Mg2+ charge compensators

The Effects of Fluxes on Aln:Eu2+ Blue Phosphors Synthesized by A Carbothermal Reduction Method

Synthesis and Luminescent Properties of CaCO 3 :Eu 3+ @sio 2 Phosphors with Core–shell Structure