Abstract:A solid-state reaction method was used to synthesize Ca2+x MgSi2Eu0.025O7+x (x = 0-1.0) powders in the air atmosphere and in a reduction atmosphere (95% N2 + 5% H2) at 1350 °C and 4 h, and the reduction atmosphere was removed at 800 °C. Only the Ca2MgSi2O7 phase was found in the XRD pattern of the synthesized Ca2MgSi2Eu0.025O7 powder. The first important discovery was that when the x value of Ca2+x MgSi2Eu0.025O7+x powders was increased from 0.2 to 0.8, both Ca2MgSi2O7 and Ca3MgSi2O8 phases coexisted in the synthesized Ca2+x MgSi2Eu0.025O7+x powders, and the diffraction intensity of the Ca2MgSi2O7 (Ca3MgSi2O8) phase decreased (increased) with the x value. The second important discovery was that the Ca2MgSi2Eu0.025O7 phosphor exhibited stronger photoluminescence excitation (PLE), photoluminescence (PL), and decay curve properties than the Ca2.2MgSi2Eu0.025O7.2 phosphor, and the Ca3MgSi2Eu0.025O8 phosphor exhibited stronger PLE, PL, and decay curve properties than the Ca2+x MgSi2Eu0.025O7+x phosphors for x = 0.4, 0.6, and 0.8. For x = 0.2-0.8, the PL spectra of the Ca2+x MgSi2Eu0.025O7+x phosphors were a combination of the PL spectra of Ca2MgSi2Eu0.025O7 and Ca3MgSi2Eu0.025O8 phosphors. The third important discovery was that as the x value was increased, the maximum emission peak wavelengths of the Ca2+x MgSi2Eu0.025O7+x phosphors shifted to a lower value, the maximum emission intensity of the PL spectra increased, and the emission light changed from green and cyan to blue.

Effects of Composition Variations on the Crystalline Phases and Photoluminescence Properties of Ca 2+ x MgSi 2 Eu 0.025 O 7+ x Phosphors

Investigations of Photoluminescence Properties of CaxMg2-xSi2O6:yEu2+ (x = 0.5–1.25, y = 0.015–0.035) Phosphors

Photoluminescence evolutions and physical mechanism discussions of Sr1.95-(Ca/Ba) MgSi2O7:Eu2+ phosphors

Enhancing the Emission Intensity and Decreasing the Full Widths at Half Maximum of Ba3Si6O12N2:Eu(2+) by Mg(2+) Doping.

Eu 3+ -doped Sr 2 (Al 1−x Mg x )(Al 1−x Si 1+x )O 7 phosphors: electronic, crystal structures and photoluminescence properties

Luminescent properties of CaMgSi2O6 and Ca2MgSi2O7 phosphors activated by Eu2+, Dy3+and Nd3+

The Effect of Eu2+ Doping Concentration on Luminescence Properties of Ca2-xMgSi2O7∶x Eu2+ Green Phosphor

Luminescence properties of CaSi2O2N2 ∶Ce3+/Eu phosphors

Cathodoluminescence Properties of Ba3Si6O9N4:Eu2+ Phosphors

Synthesis, structure, and luminescence properties of SrSiAl<sub>2</sub>O<sub>3</sub>N<sub>2</sub>:Eu<sup>2+</sup> phosphors for light-emitting devices and field emission displays

The Effect of Doping Mg2+ on Structure and Properties of Sr(1.992-x)MgxSiO4: 0.008eu(2+) Blue Phosphor Synthesized by Co-Precipitation Method

Crystal Structure Evolution and Luminescence Properties of Color Tunable Solid Solution Phosphors Ca2+Xla8-X(Sio4)(6-X)(Po4)(X)O-2:Eu2+

Er3+ Co-Doped Sr1.956MgSi2O7: 0.004eu2+, 0.04dy3+ Phosphors and Enhancement of Luminescent Properties

Systematic studies on Ca19M2(PO4)14:Eu3+ (M = Mg, Zn) phosphors: Effects of M cation on photoluminescence

Effect of Flux on the Composition and Luminescent Properties of Ca 0.68 Mg 0.2 SiO 3 :0.12Eu 3+ Red Phosphor

Optical Properties and Electronic Structures of Eu~(2+) Doped Ca-α-SiAlON and Mg-α-SiAlON Phosphors

Luminescence investigation of Lu2MgAl4SiO12:Ce3+ and Ca2+ substituted Lu2MgAl4SiO12:Ce3+ phosphors

Intriguing Luminescence Properties of (ba, Sr) 3 Si 6 O 9 N 4 : Eu 2+ Phosphors Via Modifying Synthesis Method and Cation Substitution

Structure and Luminescence Properties Study of Eu2+ Doped Ca2Al2−xSi1+xO7−xNx Phosphors Based on Size-Mismatch Model

Effect of Eu2+ on the luminescence properties of Ba1.52−xZn0.2Li0.4SiO4:0.05Ce3+, 0.03Mn2+, xEu2+ phosphor

The luminescent properties and crystal structure of Sr (1.5-x)-(1.5y) Mg 0.5 SiO 4 :xEu 2+ ,yCe 3+ blue phosphor synthesized by co-precipitation method.