Oxidative ablation behavior of W‐coated C/C composites prepared by CVD with heat‐treatment
Zhe Zhou,Chuangfang Tao,Bin Chen,Huanyi Liao,Weiguo Mao,Zexu Sun,Xizhi Fan,Zheqiong Fan,Yuan Cheng
DOI: https://doi.org/10.1002/adem.202201781
IF: 3.6
2023-03-26
Advanced Engineering Materials
Abstract:To improve the ablation resistance of C/C composites, tungsten (W) coating is applied by chemical vapor deposition technology (CVD) on C/C composites. Results show that the coatings are dense, with a thickness of about 400 μm. After heat‐treatment at a temperature of 1500 °C for 1 h, the main component of coating is W2C. Additionally, a dense WC layer forms on the surface of pyrolytic carbon (PyC). The sample subjected to heat‐treatment remains relatively intact after ablation at 3000 °C for 60 s, with a mass and linear ablation rate of 1.83×10‐5 g·s−1 and 3.03×10‐5 cm·s−1, respectively. The high‐temperature stability of WC formed on PyC and the filling of fiber gaps to prevent oxygen penetration are the main reasons for the improved ablation resistance of W‐coated C/C composites. This article is protected by copyright. All rights reserved.
materials science, multidisciplinary