Abstract:<p>Different from traditional ceramic materials, three-dimensional (3D) porous ceramics have become a research hotspot in recent years due to combinative of light-weight and high strength. Meanwhile, the 3D printing technique, which can be used to design hierarchical porous structures by combining flexible design and advanced manufacturing procedures, is regarded as a revolutionary and attractive tool for the preparation of 3D porous ceramics. Herein, a novel road is reported for fabricating 3D porous ceramic lattices with excellent mechanical properties by bridging 3D printing and SiC chemical vapor infiltration. The effects of coordination number, rotation angle, hollow structure and sintering temperature on the performance of ceramic lattices were also investigated. As revealed by the results, the cubic lattices possess the highest compressive strength and fracture work, 41.93 MPa and 2126.7 kJ/m<sup>2</sup>, respectively. Among different hollow lattices, the stability and bearing capacity of triangular structures were superior to that of square and honeycomb structures. The compressive strength of the triangular hollow lattices can reach up to 31.20 MPa. And the fracture work of the 3D porous lattices without rotation can be 7 times that of the lattices with a rotation angle of 30° and 45°. Moreover, as the sintering temperature rises, the compressive strength of 3D porous ceramics gradually increases while the shrinkage tends to be more serious. Additionally, the fracture work of 3D porous ceramics reaches its peak at a sintering temperature of 1400 °C. The approach developed in this work provides a simple, economic, and effective way to fabricate 3D porous ceramics, which leads to promising applications in future functional devices.</p>

Three-dimensional printing of Ti3SiC2-based ceramics

Si3N4-SiC Composite Ceramic Prepared by Three Dimensional Printing and Chemical Vapor Infiltration

Freeform Fabrication of Ti3SiC2 Powder-Based Structures

Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

Preparation and properties of Ti3SiC2 preform reinforced SiC ceramic matrix composites

Fabrication of Si3N4–SiC/SiO2 composites using 3D printing and infiltration processing

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

3D printing of porous SiC ceramics added with SiO2 hollow microspheres

Mechanical and dielectric properties of porous and wave-transparent Si3N4-Si3N4 composite ceramics fabricated by 3D printing combined with chemical vapor infiltration

Freeform Fabrication of Ti3SiC2 Structures

PREPARATION OF TiC/SiC AND TiN/SiC COMPOSITE CERAMICS FROM LIQUID SILICON INFILTRATION

Preparation and Thermal-Physical Properties of Three Dimensional Bicontinuous SiC/Cu-Si Composite

High-strength and low-silicon SiC ceramics prepared by extrusion molding 3D printing

Microstructures, Mechanical Properties and Electromagnetic Wave Absorption Performance of Porous SiC Ceramics by Direct Foaming Combined with Direct-Ink-Writing-Based 3D Printing

Three-dimensional printing of SiCN ceramic matrix composites from preceramic polysilazane by digital light processing

Effect of Chemical Vapor Infiltration of Si3n4 on the Mechanical and Dielectric Properties of Porous Si3n4 Ceramic Fabricated by A Technique Combining 3-D Printing and Pressureless Sintering

A Novel In-Situ Synthesis Route of Ti3SiC2-SiC Composite by Liquid Silicon Infiltration

Structure design influencing the mechanical performance of 3D printing porous ceramics

Mechanical and Dielectric Properties of 3D Printed Highly Porous Ceramics Fabricated Via Stable and Durable Gel Ink

Fabrication of 3D-SiC/aluminum alloy interpenetrating composites by DIW and pressureless infiltration

Fabrication of High‐strength Porous SiC‐based Composites with Unidirectional Channels