Abstract:The corrosion behavior of functionally graded cemented carbide (FGCC), with CoNiCrFe binder (WC-CoNiCrFe), has been investigated by performing electrochemical measurements and chemical characterization. The results showed that the CoNiCrFe binder was selectively dissolved in alkaline and acidic solutions. In the NaOH solution, the high contents of Ni and Co generated a passive film consisting of Co(OH) 2 , Ni(OH) 2 , Co 3 O 4 , and NiO that effectively isolated the corrosive medium from the materials. However, the contents of Fe and Cr were too low to provide satisfactory protection. In the HCl solution, the Cr element generated Cr 0 , Cr 2 O 3 , and Cr(OH) 3 . However, the Cr content was too low to form a passive film. In addition, Co, Ni and Fe in the binder were selectively dissolved in the acidic solution. Moreover, compared with the FGCC, the non-graded cemented carbide (CC) had a higher binder content and a more dispersed WC distribution. Thus, it formed a denser and thicker passive film, which was beneficial for the corrosion resistance in the NaOH solution. However, the CoNiCrFe binder was severely corroded in the HCl solution, which was due to the absence of a passive film. In comparison, the FGCC with a lower binder content and a denser WC distribution, showed a higher corrosion resistance. On the other hand, the WC grain size showed the opposite effect in alkaline and acidic solutions. In the NaOH solution, a small WC grain size increased the number of WC/CoNiCrFe interfaces, which favored the formation of a dense passive film. It, thereby reduced the probability for pitting corrosion. In the HCl solution, the corrosion generally started from grain boundaries with high interface energy as no passive film existed. Thus, a large WC grain size facilitated the improvement of the corrosion resistance. The results from the present study do not only provide a theoretical guidance for an understanding of the anticorrosion mechanism of WC-CoNiCrFe, but also a new approach for the preparation of cemented carbides with high corrosion resistance.

Electrochemical Corrosion Behaviors of Binderless Carbides

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

Comparative Study of Corrosion Behaviors of WC-NiMo and WC-Co Cemented Carbides

Corrosion behavior of functionally graded cemented carbides with CoNiCrFe binder

WC-(7-9)Ni-(1-2)Cr Hard Alloy Anticorrosion Performance Research

Corrosion Resistance Enhancement of WC Cermet Coating by Carbides Alloying

Study on Effect of High-Entropy Alloy Binder on Microstructure and Properties of WC Cemented Carbide Doped with Rare Earth Oxide

Influence of Ni and Cr on Anti-corrosion Performance of Tungsten Carbide Base Hard Alloy

Tribocorrosion behavior of HVOF sprayed WC-based cermet coatings in sodium chloride solution environment in relation to binder phases

Electrochemical corrosion behavior of hot-pressing sintered WC-Al2O3 composite in alkaline and acidic solutions

TEM and ToF-SIMS studies on the corrosion behavior of vanadium and chromium containing WC–Co hard metals in alkaline solutions

Cold-sprayed Cu Matrix Composite Coatings with Core-Shell Structured Co@WC Reinforcements on Q235 Steel

The optimization of mechanical property and corrosion resistance of WC-6Co cemented carbide by Mo2C content

Effect of Cr3C2 Addition on Microstructure and Mechanical Properties of WC-CoNiFe Cemented Carbides

Prediction of hardmetal corrosion based on the binder response

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

The Effect of Carbon Content on the Microstructure and Mechanical Properties of Cemented Carbides with a CoNiFeCr High Entropy Alloy Binder

The effect of binder phase content on WC-AlCoCrFeNiTi0.2 high entropy cemented carbides microstructure and mechanical properties

Influences of Cr contents on oxidation behavior of WC-Co-Ni-Cr cemented carbides at 900 °C

Corrosion Properties and Tribological Behavior of Tungsten Carbide Coatings with Alumide Matrix of SS AISI304