Improvement of microstructure and properties of Ni coating prepared by high frequency pulsed-electrodeposition

WANG Zi-han,YANG Bin,JIANG Chun-li,WANG Qing-fu,ZHANG Peng-cheng,FAN Ai-ping
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2011.04.018
2011-01-01
Abstract:The effects of pulse frequency on the microstructure, corrosion and wear resistance properties of a nanocrystalline Ni coating produced by high frequency pulsed-electrodeposition technique were studied. The corrosion behavior of the Ni deposit was also evaluated by polarization curves and electrochemical impedance spectroscopy (EIS) in 50 μg/g potassium chloride aqueous solution with at room temperature. The results show that the grain size of the Ni coating is refined with the increase of pulse frequency from 30 to 100 kHz. The charge transfer resistance and self-corrosion potential of the coating are increased from 1.97×104 to 6.56×104 Ω·cm2 and from -551.41 to -420.28 mV, respectively with increasing frequency from 30 to 100 kHz, revealing that the corrosion resistance of the Ni coating is improved owing to its grain-refinement and higher compactness. The tribological tests show that the friction coefficient of the Ni coating decreases from 0.39 to 0.25 with frequency increasing from 30 to 100 kHz. The reason is suggested to its grain-refinement, higher compactness and microhardness.
What problem does this paper attempt to address?