Abstract:Lead-free (1 - x)(0.96K(0.46)Na(0.54)Nb(0.98)Ta(0.02)O(3)-0.04Bi(0.5)(Na0.82K0.18) 0.5ZrO3)-xCaZrO(3) ((1 - x)(0.96KNNT-0.04BNKZ)-xCZ) piezoelectric ceramics were prepared by the conventional solid-state reaction method. The CaZrO3 dopant can induce a coexisting phase boundary with the transition from the orthorhombic/tetragonal phase to the R phase. Domains that exist across the grain boundary within neighboring grains appear in the ceramics with x = 0.01, which can result in an increase in ferroelectricity due to its long-range order organization. The CaZrO3 dopant results in the formation of polar nanodomains and induces the appearance of diffuse ferroelectrics. The ceramics with x = 0.01 show optimal piezoelectric properties (d(33) = 300 pC N-1 and d*(33) = 500 pm V-1 at 25 kV cm(-1)). Meanwhile, their high level of unipolar strain reaches up to 0.175% at 35 kV cm(-1) at room temperature, and their field-induced strain varies less than 10% from room temperature to 120 degrees C. The ceramics with x = 0.02 possess a remarkably high temperature stability of d*(33) (T-e = 200 degrees C). For x = 0.005-0.025, a higher amount of the CaZrO3 dopant can obviously improve the temperature stability of d*(33): The (1 - x)(0.96KNNT-0.04BNKZ)-xCZ system is a promising lead-free piezoelectric candidate material for commercial applications.

Low-Temperature Sintering of ZnO and B2O3 Co-Doped (k0.5na0.5)nbo3 Lead-Free Piezoelectric Ceramics

Low-Temperature Sintering of ZnO and B<sub>2</sub>O<sub>3</sub> Co-Doped (K<sub>0.5</sub>Na<sub>0.5</sub>)NbO<sub>3</sub> Lead-Free Piezoelectric Ceramics

Low‐Temperature Sintering of CuO‐Doped 0.94(k0.48na0.535)nbo3–0.06linbo3lead‐free Piezoelectric Ceramics

New K0.48Na0.52NbO3–Bi(Zn0.5Zr0.5)O3 Lead-Free Ceramics: Microstructure and Piezoelectricity

(Bi0.5na0.5)(zr0.97w0.01fe0.02)o3 Doping Effects on KNN‐based Lead‐free Ceramics Prepared Via Two‐step Sintering Technique

Effect of Sintering Temperature on Microstructure and Electric Properties of 0.95(k0.5na0.5)nbo3–0.05li(nb0.5sb0.5)o3with Copper Oxide Sintering Aid

Piezoelectric Properties of Low-Temperature Sintered Li-Modified (na, K)Nbo3 Lead-Free Ceramics

Low temperature sintering and enhanced piezoelectricity of lead-free (Na 0.52 K 0.4425 Li 0.0375)(Nb 0.86 Ta 0.06 Sb 0.08) O 3 ceramics prepared from nano-powders

Sintering and Electrical Properties of Lead-Free Na0.5k0.5nbo3 Piezoelectric Ceramics

Preparation of KNN Based Lead-Free Piezoelectric Ceramics Via Composition Designing and Two-Step Sintering

Low-Temperature Sintering of (K0.5Na0.5)NbO3-FeTiO3 Lead-Free Piezoelectric Ceramics

Microstructure and Piezoelectric Properties of CuO-doped 0.95(k0.5na0.5)nbo3–0.05li(nb0.5sb0.5)o3 Lead-Free Ceramics

Enhanced piezoelectric properties in 0.96(K0.48Na0.52)(Nb1−xTax)O3–0.04(Bi0.5Ag0.5)ZrO3 lead-free ceramics

Low‐Temperature Sintering of Li‐Modified (K, Na)NbO3 Lead‐Free Ceramics: Sintering Behavior, Microstructure, and Electrical Properties

Effects of Sintering Temperature and Alkaline Elements Excess on the Structure and Electrical Properties of (k0.462na0.48li0.058)1+xnbo3 Lead-Free Piezoelectric Ceramics

Normal Sintering of (K, Na)Nbo3-Based Lead-Free Piezoelectric Ceramics

Low‐Temperature Sintering of Lead‐Based Piezoelectric Ceramics

Enhanced Dielectric and Piezoelectric Properties in Li/Sb-modified (na, K)NbO3 Ceramics by Optimizing Sintering Temperature

Sintering properties of K_(0.5)Na_(0.5)NbO_3 lead-free piezoelectric ceramics

A high temperature stable piezoelectric strain of KNN-based ceramics

Low-temperature Sintering of (K,na)nbo3-Based Lead-Free Piezoceramics with Addition of LiF