Characteristics and transformation of primary carbides during austenitization in Cr4Mo4V bearing steel
Weifeng Liu,Yanfei Cao,Yifeng Guo,Bin Xu,Mingyue Sun,Dianzhong Li
DOI: https://doi.org/10.1016/j.matchar.2020.110636
IF: 4.537
2020-11-01
Materials Characterization
Abstract:<p>The characteristics and transformation of M<sub>2</sub>C and MC, the most common primary carbides in Cr4Mo4V bearing steel, have been investigated via scanning electron microscopy, energy dispersive spectrometry and X-ray diffraction at high austenitization temperatures. It was first found that the transformation of rod-like M<sub>2</sub>C and spherical MC primary carbides during heating occurs at approximately 1180 and 1200 °C, respectively. In the transformation process of M<sub>2</sub>C, the periphery first transforms into an MC-type carbide, and then the internal untransformed M<sub>2</sub>C and newly-formed MC-type melt, and re-solidify in a M<sub>2</sub>C<sup>"</sup> eutectic carbide structure with a composition change and a finer lamellar spacing. In contrast, MC carbides melt directly with the re-solidified product also being constituted of finer M<sub>2</sub>C<sup>"</sup> eutectic carbides. The transformation process is controlled by the diffusion of alloying elements Mo and V, while the matrix provides Fe for the formation of M<sub>2</sub>C<sup>"</sup>. In addition to elucidate the transformation mechanisms, this study also highlights the essential effect of the melting matrix on the modification of primary M<sub>2</sub>C and MC carbides in Cr4Mo4V steel.</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing