Abstract:Three ion-typed surfactants, including anionic sodium dihexyl sulfosuccinate (SDSS), cationic ammonium salt of poly(ethylene glycol) (ASPEG) and non-ionic poly(ethylene glycol) (PEG), were added to 10 wt% tetramethyl ammonium hydroxide water (TMAHW) solutions to evaluate the silicon anisotropic etching properties of the (1 0 0) silicon plane without agitation and no isopropyl alcohol (IPA) additive. The results indicate that the wetting capacity of the etchants cause the efficacies of the etchants on the roughness reduction to follow the order cationic ASPEG, non-ionic PEG, pure solution and anionic SDSS in TMAHW solutions, especially at high etching temperatures. Moreover, the chemical activities of the etchants cause the efficacies of the etchants on the etching rates to follow the order anionic SDSS, pure solution, cationic ASPEG and non-ionic PEG in TMAHW solutions at a given etching temperature. The cationic ASPEG has a reasonable etching rate of 0.7 µm min−1 and the lowest surface roughness of 4 nm in TMAHW solutions at an etching temperature of 100 °C. ASPEG and PEG in TMAHW solutions markedly affect aluminum passivation. The undercutting of the convex corners in PEG-added TMAHW solutions can be drastically reduced without using corner compensation; the undercutting ratio obtained using a PEG surfactant is about 45% lower than that obtained in pure TMAHW solution. This finding reveals that non-ionic PEG should be added to TMAHW solutions when accurate profiles are required without extremely deep etching. This study also demonstrated that non-ionic PEG is more appropriate than IPA for anisotropic silicon TMAHW etching.

Effects of IPA on texturing process for mono-crystalline silicon solar cell in TMAH solution

A Simple Texturization Approach for Mono-Crystalline Silicon Solar Cell with Low Tmah Concentration Solution

Texturization of Mono-Crystalline Silicon Solar Cells in TMAH Without the Addition of Surfactant

Investigation of Texturing Industrial Mono-Crystalline Silicon Solar Cells

Investigation of Texturization for Monocrystalline Silicon Solar Cells with Different Kinds of Alkaline

Effects of Different Alcohols on Texture Properties of Monocrystalline Silicon

TEXTURIZATION OF MONOCRYSTALLINE SILICON FOR SOLAR CELLS

Effect of additives on the anisotropic etching of silicon by using a TMAH based solution

Effect of Isopropyl Alcohol Concentration and Etching Time on Wet Chemical Anisotropic Etching of Low-Resistivity Crystalline Silicon Wafer

INFLUENCE OF SUB-SURFACE DAMAGE ON TEXTURING OF MONOCRYSTALLINE SILICON WAFERS FOR SOLAR CELLS

Effects of PEAI Post-treatments on the Ion Migration in Lead Iodide Perovskites

Electrochemical Oxidation Pre-Treatment for Wet Texturing of Monocrystalline Silicon Solar Cells

Research of Texturization on Multi-crystalline Silicon Surface for Solar Cell

Effect of tetramethylammonium hydroxide/isopropyl alcohol wet etching on geometry and surface roughness of silicon nanowires fabricated by AFM lithography

The Effects of TMDD-PA Concentration on Roughness of Si 〈1 1 0〉 and Etching Rate Ratio of Si 〈1 1 0〉/〈1 1 1〉 in Alkaline KOH Solution

Acid Texturing of Large Area Multi-Crystalline Silicon Wafers for Solar Cell Fabrication

Influences of Temperature and Concentrations on Morphology of Tmah Anisotropic Etching for Silicon Microchannel Plate

Study on anisotropic silicon etching characteristics in various surfactant-added tetramethyl ammonium hydroxide water solutions

Effects of etching conditions on surface morphology of periodic inverted trapezoidal patterned Si(100) substrate

Enhanced Efficiency of Graphene-Silicon Schottky Junction Solar Cell through Pyramid Arrays Texturation

Improvement of conversion efficiency of multicrystalline silicon solar cells by incorporating reactive ion etching texturing