Abstract:Vanadia-based catalysts have been widely used for catalyzing various reactions, including their long-standing application in the deNOx process. It has been commonly considered that various vanadium species dispersed on supports with a large surface area act as the catalytically active sites. However, the role of crystalline V2O5 in selective catalytic reduction of NOx with NH3 (NH3-SCR) remains unclear. In this study, a catalyst with low vanadia loading was synthesized, in which crystalline V2O5 was deposited on a TiO2 support that had been pretreated at a high temperature. Surprisingly, the catalyst, which had a large amount of crystalline V2O5, showed excellent low-temperature NH3-SCR activity. For the first time, crystalline V2O5 on low-vanadium-loading catalysts was found to be transformed to polymeric vanadyl species by the adsorption of NH3. The generated active polymeric vanadyl species played a crucial role in NH3-SCR, leading to remarkably enhanced catalytic performance at low temperatures. This new finding provides a fundamental understanding of the metal oxide-catalyzed chemical reaction and has important implications for the development and commercial applications of NH3-SCR catalysts.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/jacs.1c05354?goto=supporting-info">https://pubs.acs.org/doi/10.1021/jacs.1c05354</a>.XRD profiles, NH3-SCR activity, effect of SO2 on NOx conversion, NH3-TPD results, in situ DRIFTS, in situ Raman spectra, DFT calculation, and plot of the change in integral area of various Raman peaks (<a class="ext-link" href="/doi/suppl/10.1021/jacs.1c05354/suppl_file/ja1c05354_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Experimental Study of Dynamic Reaction and Ammonia Storage Characteristics of Vanadium-Based SCR Catalyst

Ammonia storage and slip in a urea selective catalytic reduction catalyst under steady and transient conditions

Experimental investigation on the characteristics of ammonia storage for heavy-duty diesel engine SCR catalyst

Experimental Study of the Selective Catalytic Reduction After-Treatment for the Exhaust Emission of a Diesel Engine

Low Temperature Selective Catalytic Reduction of NO and NO2 with NH3 over Activated Carbon-Supported Vanadium Oxide Catalyst

Experimental demonstration of NOx reduction and ammonia slip for diesel engine SCR system

Experimental Study of Ammonia Slip of Diesel Engine Urea Selective Catalytic Reduction System in Transient Condition

Influence of Urea-SCR System Parameters on NOx Conversion Rate and Liquid Film

Recent Progress on Improving Low-Temperature Activity of Vanadia-Based Catalysts for the Selective Catalytic Reduction of NOx with Ammonia

Ammonia storage and slip under steady and transient state in close-coupled SCR

Effect of Treatment Atmosphere on the Vanadium Species of V/TiO2 Catalysts for the Selective Catalytic Reduction of NOx with NH3

Study of Low-Temperature Selective Catalytic Reduction of NO by Ammonia over Carbon-Nanotube-supported Vanadium

Effect of Vanadium-Based Selective Catalytic Reduction Catalysts on Mercury Speciation Transformation

Study on the Removal of NOX from Sintered Flue Gas by Vanadium Sintered Ore

Active Vanadium(IV) Species Synthesized at Low-Temperature Facilitate Excellent Performance in Low-Temperature NOx-Catalytic Removal

Ammonium Ion Enhanced V2O5-WO3/TiO2 Catalysts for Selective Catalytic Reduction with Ammonia

Study on the SCR Properties of Vanadium-based De-NOx Catalyst at Mid-low Temperature

Influence of Calcination Temperature over Vanadium–Molybdenum Catalysts for the Selective Catalytic Reduction of NOx with NH3

Adsorption-Induced Active Vanadium Species Facilitate Excellent Performance in Low-Temperature Catalytic NO x Abatement

Dynamic Change of Active Sites of Supported Vanadia Catalysts for Selective Catalytic Reduction of Nitrogen Oxides

Effect of MoO3 on Vanadium Based Catalysts for the Selective Catalytic Reduction of NOx with NH3 at Low Temperature.