Abstract:Vanadia-based catalysts have been widely used for catalyzing various reactions, including their long-standing application in the deNOx process. It has been commonly considered that various vanadium species dispersed on supports with a large surface area act as the catalytically active sites. However, the role of crystalline V2O5 in selective catalytic reduction of NOx with NH3 (NH3-SCR) remains unclear. In this study, a catalyst with low vanadia loading was synthesized, in which crystalline V2O5 was deposited on a TiO2 support that had been pretreated at a high temperature. Surprisingly, the catalyst, which had a large amount of crystalline V2O5, showed excellent low-temperature NH3-SCR activity. For the first time, crystalline V2O5 on low-vanadium-loading catalysts was found to be transformed to polymeric vanadyl species by the adsorption of NH3. The generated active polymeric vanadyl species played a crucial role in NH3-SCR, leading to remarkably enhanced catalytic performance at low temperatures. This new finding provides a fundamental understanding of the metal oxide-catalyzed chemical reaction and has important implications for the development and commercial applications of NH3-SCR catalysts.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/jacs.1c05354?goto=supporting-info">https://pubs.acs.org/doi/10.1021/jacs.1c05354</a>.XRD profiles, NH3-SCR activity, effect of SO2 on NOx conversion, NH3-TPD results, in situ DRIFTS, in situ Raman spectra, DFT calculation, and plot of the change in integral area of various Raman peaks (<a class="ext-link" href="/doi/suppl/10.1021/jacs.1c05354/suppl_file/ja1c05354_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Study of Low-Temperature Selective Catalytic Reduction of NO by Ammonia over Carbon-Nanotube-supported Vanadium

Low Temperature Selective Catalytic Reduction of NO and NO2 with NH3 over Activated Carbon-Supported Vanadium Oxide Catalyst

Adsorption-Induced Active Vanadium Species Facilitate Excellent Performance in Low-Temperature Catalytic NO x Abatement

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Recent Progress on Improving Low-Temperature Activity of Vanadia-Based Catalysts for the Selective Catalytic Reduction of NOx with Ammonia

New Insight into Alkali Resistance and Low Temperature Activation on Vanadia-Titania Catalysts for Selective Catalytic Reduction of NO

Low temperature selective catalytic reduction of NOx by NH3 over Cu modified V2O5/TiO2–carbon nanotube catalyst

Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes

Low-temperature Selective Catalytic Reduction of NO with NH3 over Nanoflaky MnOx on Carbon Nanotubes in Situ Prepared Via a Chemical Bath Deposition Route

Active Vanadium(IV) Species Synthesized at Low-Temperature Facilitate Excellent Performance in Low-Temperature NOx-Catalytic Removal

In Situ DRIFTS Investigation on the SCR of NO with NH3 over V2O5 Catalyst Supported by Activated Semi-Coke

Synergy of vanadia and ceria in the reaction mechanism of low-temperature selective catalytic reduction of NOx by NH3

In Situ Supported Mnox-Ceox On Carbon Nanotubes For The Low-Temperature Selective Catalytic Reduction Of No With Nh3

Time-resolved in-situ IR and DFT study: NH<sub>3</sub> adsorption and redox cycle of acid site on vanadium-based catalysts for NO abatement via selective catalytic reduction

Low-Temperature Scr of No with Nh3 over Activated Semi-Coke Composite-Supported Rare Earth Oxides

Selective Catalytic Removal of High Concentrations of NOx at Low Temperature

Low temperature selective catalytic reduction of nitric oxide with an activated carbon-supported zero-valent iron catalyst

Uncovering the Dinuclear Mechanism of NO 2 -Involved NH 3 -SCR over Supported V 2 O 5 /TiO 2 Catalysts

Improvement in Activity and Alkali Resistance of a Novel V-Ce(SO4)2/Ti Catalyst for Selective Catalytic Reduction of NO with NH3

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3