Abstract:A reciprocating extrusion process was developed to consolidate 6061-Al 2 O 3 p composites from mixed powders. The 6061 alloy powder was first dehydrated in a vacuum chamber at 450 °C and then mixed with 12.5 µm Al 2 O 3 powder in various volume fractions: 0, 5, 10, 20, and 30 pct. The mixed powders were hot pressed at 300 °C under a pressure of 300 MPa and finally extruded reciprocatingly 14 times at 460 °C. The results show that the composites were fully densified, with no sign of pores or oxide layers observable in the optical microscope. The Al 2 O 3 particles were distributed uniformly in the matrix. As compared with 6061 alloys, the composites demonstrated a smaller precipitation hardening and elongation, but exhibited a higher Young’s modulus and a larger work hardening capacity. The degradation of precipitation hardening was due to the loss of Mg, which reacts with Al 2 O 3 to form MgAl 2 O 4 . The large work-hardening capacity is attributable to the incompatibility between Al 2 O 3 and the matrix, which possibly generates more dislocations to harden the matrix. The composites had much higher friction coefficients and greater wear resistances than the 6061 alloy against steel disc surface. The friction coefficient of the 6061-30 vol pct Al 2 O 3 p composite was double that of the 6061 alloy and the wear resistance was 100-fold. As compared with similar composites reported previously, these composites possessed much higher elongation at the same strength level. A 30 vol pct Al 2 O 3 p still displayed an elongation of 9.8 pct in the T6 condition. All of these improvements are attributed to the merits, including full densification of the bulk, uniform dispersion of the Al 2 O 3 particles in the matrix, and strong binding between the Al 2 O 3 particles and the matrix resulting from reciprocating extrusion.

Effect of Sno2 Coating on the Low Temperature Extrusion of 6061al Matrix Composite Reinforced with Aluminum Borate Whisker

MICROSTRUCTURES AND PROPERTIES OF HOT-EXTRUDED SiCW/6061Al COMPOSITES

Forming process of hot-extruded SiCw/6061AI composites(I)

Effect of coating Al2O3 reinforcing particles on the interface and mechanical properties of 6061 alloy aluminium matrix composites

Microstructure and Mechanical Properties of ABOw and Nickel-Coated MWCNTs Reinforced 2024al Hybrid Composite Fabricated by Squeeze Casting

Rare-Earth Oxide Coating for Sub-Micro Particulates Reinforced Aluminum Matrix Composites

Effect of Al2O3 coating thickness on microstructural characterization and mechanical properties of continuous carbon fiber reinforced aluminum matrix composites

The effect of SnO2 additive on the densification, microstructure and mechanical properties of MgAl2O4–CaAl12O19 composites

Preparation of Chromium Oxide Coatings on Aluminum Borate Whiskers by a Hydrothermal Deposition Process

Microstructure and property evolution of aluminium/potassium titanate whiskers composite during Rheo-casting

Effect of surface modification of Al2O3 powder with Y2O3 on microstructure and tensile properties of aluninium matrix composites

Study of 6061-Al2o3p Composites Produced by Reciprocating Extrusion

Effects of Extrusion Temperature on the Properties of a 0.5 wt% GNP/Al Composite in Porthole Die Extrusion

Aging behavior and tensile properties of 6061Al–0.3 μm Al2O3p particle composites produced by reciprocating extrusion

Mechanical behavior of Y 2 O 3 -coated Al 2 O 3p /6061 Al composites

Effect of hot extrusion on the microstructure and mechanical properties of SiCNWs/Mg-2Zn-0.1Y composite

Effects of Oxide Fragments on Microstructure and Mechanical Properties of AA6061 Aluminum Alloy Tube Fabricated by Thermomechanical Consolidation of Machining Chips

High Strength Al(2)O(3)P/6061 Al Composites: Effect Of Particles, Subgrains And Precipitates

Preparation of Al2O3 coating on Nb fiber and the effect on interfacial microstructure of Nbf/TiAl composite

High Strength Al–Al2O3p Composites: Optimization of Extrusion Parameters

Effect of Al on the Microstructure and Mechanical Properties of Mg–Sn–Ca–Mn Wrought Alloy