Abstract:Carbon nanofibers (CNFs) were synthesized by CO disproportionation on iron catalyst at CO concentration between 58.3% and 75.0%, H2 concentration between 8.3% and 25.0% and reaction temperature between 833 and 913K. The time-depending rate of CNFs growth as a function of time was determined by an on-line mass spectrometer and the morphologies of all CNFs products were observed by electronic microscopy. Not only the CNFs growth rate but also the morphology of the grown CNFs were shown to vary with the three operating variables. SEM and TEM images showed that the three-dimensional morphologies of the CNFs were twist, helical or straight and an interesting relationship between the maximal growth rate and the morphology was observed. When the growth rate was between 0.8 and 0.9mmol/(sgcat), the CNFs were twist. As the growth rate increased to 1.0mmol/(sgcat), more helical nanofibers appeared. Straight nanofibers were produced when the growth rate reached the level of 1.2mmol/(sgcat). Finally when the rate of CNFs growth was high at 1.8mmol/(sgcat), the absolute majority of the solid products was amorphous carbon coexisting with some short and thick nanofibers. Under different operating conditions, the crystal faces of the catalysts had different anisotropy properties for carbon deposition, thus producing CNFs with different morphologies.

Synthesis of Carbon/Carbon Core/Shell Nanofibers by Co-Pyrolysis of Tetrahydrofuran and Ferrocene

Synthesis of Carbon–fe3o4 Coaxial Nanofibres by Pyrolysis of Ferrocene in Supercritical Carbon Dioxide

Synthesis and Characterization of Fe/C Core–shell Nanoparticles

Synthesis and Magnetic Properties of Fe3O4/helical Carbon Nanofiber Nanocomposites from the Catalytic Pyrolysis of Ferrocene

Synthesis and Characterization of Carbon Fibrils Formed by Stacking Graphite Sheets of Nanometer Thickness

Preparation of Carbon Nanofibers over Carbon Nanotube-Nickel Catalyst in Propylene Decomposition

Single Walled 0.4 Nm Carbon Nanotube Bundles Prepared By Pyrolysis Of N-Hexane Catalyzed By Ferrocene

Large-Scale and Selective Synthesis of Carbon Nanofiber Bundles, Curved Carbon Nanofibers and Helical Carbon Nanofibers.

Pyrolytic Synthesis of Conical Carbon Fibers with Carbon Nanotube Tips on Carbon Substrates

Production of novel amorphous carbon nanostructures from ferrocene in low-temperature solution

Kinetically Controlled Synthesis of Carbon Nanofibers with Different Morphologies by Catalytic CO Disproportionation over Iron Catalyst

Catalytic Growth of Very Long Composite Nanofibres Containing Co (or Fe, Ni), SrO and Trace Carbon

Solvothermal Preparation of Amorphous Carbon Nanotubes and Fe/C Coaxial Nanocables from Sulfur, Ferrocene, and Benzene

Preparation of carbon nanofibers by the floating catalyst method

Carbon Nanofibers: Synthesis, Characterization, and Electrochemical Properties

Formation of coal-based carbon nanotubes by Fe-K catalyst

Synthesis and Characterizations of Amorphous Carbon Nanotubes by Pyrolysis of Ferrocene Confined Within Aam Templates

Synthesis Of Cobaltferrite-Dispersed Carbons By Pressure Pyrolysis Of Organometallic Copolymers

Preparation of Millimeters long Carbon Fibers Array

Controllable and Large-Scale Synthesis of Carbon Nanofibers, Bamboo-Like Nanotubes, and Chains of Nanospheres over Fe/Sno2 and Their Microwave-Absorption Properties

Selective Synthesis of Magnetic Fe<sub>2</sub>P/C and FeP/C Core/Shell Nanocables